Preparation and adsorption denitrification of heteroatoms mesoporous molecular sieve Co-MCM-41

Hong-an Xi

Abstract:The MCM-41 and Co-MCM-41 molecular sieves,prepared by hydrothermal synthesis method,were characterized with X-ray diffraction( XRD),Fourier transform infrared spectrum( FT-IR),nitrogen adsorption and NH3-TPD. The effects of aging time,crystallization temperature,crystallization time on the crystallization process of MCM-41 and Co-MCM-41 molecular sieves were investigated. The optimal conditions were as follows: 1 h of aging time,110 ℃ of crystallization temperature and 2 d of crystallization time. XRD and FT-IR results indicated that Co was introduced into the framework of MCM-41. Brunauer-Emmett-Teller( BET)surface area and pore volume of MCM-41 and Co-MCM-41 were 986. 42 m2/ g,637. 69 m2/ g,0. 762 1 m3/ g and 0. 537 2 m3/ g respectively. The average pore diameter was 2. 82 nm for both of MCM-41 and Co-MCM-41.The results of TPD showed that although MCM-41 and Co-MCM-41 possessed weak acidity,the acidity of Co-MCM-41 was stronger than MCM-41. Denitrification of model fuels containing about 1 737. 35 μg(nitrogen) /g(16. 03 mg(quinoline) /g) was studied over the synthesized MCM-41 and Co-MCM-41 with static adsorption at ambient conditions. The molecular size of quinoline,calculated by using density functional theory(DFT),was 0. 711 6 nm × 0. 500 2 nm,implying that the quinoline easily access to the mesopores of MCM-41 and Co-MCM-41. The removal rate of basic nitrogen by Co-MCM-41 was clearly higher than MCM-41 due to its strong acidity and chemisorption between Co-MCM-41 and quinoline. Furthermore,Co-MCM-41 could be easily regenerated.

Environmental Science,Chemistry,Materials Science