Abstract:The commercial bleached bamboo was oxidized to TEMPO-oxidized cellulose nanofibrils (TOCNs) with hundreds of nanometers in length, less than 5 nm in width and the thickness less than 1 nm, which was done through TEMPO (2,2,6,6-tetramethylpiperidine-1-oxyl radical)-mediated oxidation and successive mild disintegration in water solution combined with high frequency ultrasonic treatment. The shape and dimensions of these sheets (termed "nanoribbons" hereafter), composed of many mono-and multi-layered molecular sheets, were analyzed by scattering and spectroscopy techniques to understand the structural changes. The morphology of the raw material and two types of TOCNs nanoribbons were characterized by field emission scanning electron microscope (FESEM). And the three-dimensional morphologies of the same two TOCNs samples were measured through transmission electron microscope (TEM) and atomic force microscope (AFM). The results revealed that the TEMPO-mediated oxidization systems processed in cellulose I-beta intra-layer hydrogen bonds and the long axis direction of elementary fibrils (composed by 36 cellulose chains), which was explained based on the three dimensional size difference and the change of the crystalline structure in TOCNs nanoribbons. The structures of different nanoribbons were analyzed by Fourier infrared absorption spectrum (FTIR), X-ray diffraction (XRD) and cross polarization and magic angle spinning solid-state C-13 nuclear magnetic resonance (CP/MAS C-13-NMR). FTIR analysis indicated that structure of the cellulose nanofibrils was changed during oxidization, significant amount of C6 carboxylate groups were selectively formed on each cellulose nanofibril surface by TEMPO-mediated oxidation without any changes to the original crystalline structure. XRD analysis indicated that the cellulose elementary fibrils were broken mainly along its (101) planes in TEMPO/NaClO/NaClO2 and TEMPO/NaClO/NaBr oxidized systems under high frequency ultrosonic treatment, while the I-beta crystalline structure was retained. CP/MAS 13C-NMR results were in accordance with the analyses from XRD and Raman spectra. Moreover, the oxidization scheme was important to explain the structures of the final products. This research has important significance for design, development and application of ultrafine biomass cellulose nanoribbons.

TEMPO-oxidized cellulose fibers from wheat straw: Effect of ultrasonic pretreatment and concentration on structure and rheological properties of suspensions

The non-trivial role of native xylans on the preparation of TEMPO-oxidized cellulose nanofibrils

High Frequency Ultrasound Preparation Of Tempo-Oxided Ultrafine Cellulose Nanofibrils Of Angstrom-Scale

Effects of the Solids Content of TEMPO-oxidized Cellulose Prior to Freeze-drying on the Properties of the Dried Materials

Characteristics and Properties of Cellulose Nanofibers Prepared by TEMPO Oxidation of Corn Husk

Effects of poly(vinyl alcohol) (PVA) concentration on rheological behavior of TEMPO-mediated oxidized cellulose nanofiber/PVA suspensions

Concentration Effects on the Isolation and Dynamic Rheological Behavior of Cellulose Nanofibers Via Ultrasonic Processing

Rheology of Suspensions of TEMPO-Oxidised and Cationic Cellulose Nanofibrils—The Effect of Chemical Pre-Treatment

Superior effect of TEMPO-oxidized cellulose nanofibrils (TOCNs) on the performance of cellulose triacetate (CTA) ultrafiltration membrane

Preparation of Ultrasonic-Assisted High Carboxylate Content Cellulose Nanocrystals by TEMPO Oxidation

Kinetic Dissolution Behavior and Mechanism of Bamboo Cellulose Fiber by TEMPO-catalyzed Oxidation

TEMPO-Mediated Oxidation Promotes Cellulose Dissolution in a Zincate–NaOH System at Suprazero Temperatures

Cost-effective preparation of highly amorphous cellulose nanofibrils with TEMPO oxidation promoted by mild molten salt hydrate pretreatment

The role of heteropolysaccharides in developing oxidized cellulose nanofibrils.

Oxidized cellulose prepared by ultrasonic coupling TEMPO system and its application in papermaking process

Enhancing the redispersibility of TEMPO-mediated oxidized cellulose nanofibrils in N,N-dimethylformamide by modification with cetyltrimethylammonium bromide

TEMPO-Mediated Oxidation of Cellulose and Preparation of Cellulose Nanofibrils

Comparative characterization of TEMPO-oxidized cellulose nanofibril films prepared from non-wood resources

Nanocellulose Film Properties Tunable by Controlling Degree of Fibrillation of TEMPO-Oxidized Cellulose

Influence of Chemical and Enzymatic TEMPO-Mediated Oxidation on Chemical Structure and Nanofibrillation of Lignocellulose