Effect of KNN substitution on the structural, electrical, and piezo characteristics of lead-free 0.94NBT–0.06SrTiO3 ceramics

DOI: https://doi.org/10.1007/s10854-024-12611-7

2024-04-25

Journal of Materials Science Materials in Electronics

Abstract:The conventional solid-state reaction approach was employed to develop 0.94NBT–0.06SrTiO 3 and 0.94NBT–0.06SrTiO 3 –KNN lead free electro ceramics. Both ceramics coexist in the rhombohedral structural phase ( R 3 c ) and tetragonal structural phase ( P 4 mm ) regions. When K 0.5 Na 0.5 NbO 3 (KNN) is introduced to 0.94Na 0.5 Bi 0.5 TiO 3 –0.06SrTiO 3 , the structure grows more symmetric without compromising electrical polarization. The surface morphology of both ceramics is measured by the average grain size, which is reduced somewhat from 3 to 2.6 μm, resulting in the influence of KNN. The composition-induced local structural transition—i.e., the change from order to disorder-occurs when KNN is added to the 0.94NBT–0.06SrTiO 3 binary system. Additionally, the depolarization temperature ( T d ) increases substantially with the inclusion of KNN. When KNN is present, the coercive field ( E c ) dramatically reduces from 32 to 21 kV/cm (~ Δ E = 11 kV/cm), without impairing the remaining remnant polarization ( P r ). When compared to 0.94NBT–0.06SrTiO 3 , the substitution of KNN produces a high strain response of roughly 0.25% (under a mild field of 60 kV/cm). The longitudinal strain value of 140pC/N was determined parallelly. As a result, both of these lead-free ceramics are attractive prospects for next-generation electro ceramic applications.

engineering, electrical & electronic,materials science, multidisciplinary,physics, condensed matter, applied