Abstract:Here we demonstrate that the photoactivity of Au-decorated TiO2 electrodes for photoelectrochemical water oxidation can be effectively enhanced in the entire UV-visible region from 300 to 800 nm by manipulating the shape of the decorated Au nanostructures. The samples were prepared by carefully depositing Au nanoparticles (NPs), Au nanorods (NRs), and a mixture of Au NPs and NRs on the surface of TiO2 nanowire arrays. As compared with bare TiO2, Au NP-decorated TiO2 nanowire electrodes exhibited significantly enhanced photoactivity in both the UV and visible regions. For Au NR-decorated TiO2 electrodes, the photoactivity enhancement was, however, observed in the visible region only, with the largest photocurrent generation achieved at 710 nm. Significantly, TiO2 nanowires deposited with a mixture of Au NPs and NRs showed enhanced photoactivity in the entire UV visible region. Monochromatic incident photon-to-electron conversion efficiency measurements indicated that excitation of surface plasmon resonance of Au is responsible for the enhanced photoactivity of Au nanostructure-decorated TiO2 nanowires. Photovoltage experiment showed that the enhanced photoactivity of Au NP-decorated TiO2 in the UV region was attributable to the effective surface passivation of Au NPs. Furthermore, 3D finite-difference time domain simulation was performed to investigate the electrical field amplification at the interface between Au nanostructures and TiO2 upon SPR excitation. The results suggested that the enhanced photoactivity of Au NP-decorated TiO2 in the UV region was partially due to the increased optical absorption of TiO2 associated with SPR electrical field amplification. The current study could provide a new paradigm for designing plasmonic metal/semiconductor composite systems to effectively harvest the entire UV visible light for solar fuel production.

Aminated TiO2 nanotube as a Photoelectrochemical Water Splitting photoanode

Balsam-Pear-Like Rutile/Anatase Core/Shell Titania Nanorod Arrays For Photoelectrochemical Water Splitting

Ni-doped TiO2 Nanotubes Photoanode for Enhanced Photoelectrochemical Water Splitting

Enhanced light-driven photoelectrochemical catalysis of water splitting by TiO 2 nanotubes grown on acid-etched titanium foils

Facile Preparation of Ti3+/Ni Co-Doped TiO2 Nanotubes Photoanode for Efficient Photoelectrochemical Water Splitting

Enhanced photoelectrochemical water splitting via hydrogenated TiO 2 nanotubes modified with Cu/CuO species

Α-Fe2o3/ti–nb–zr–o Composite Photoanode for Enhanced Photoelectrochemical Water Splitting

Photoactive Anode of NiO/TiO2 Nanotube P-N Junctions and Application in Photoassisted Water Electrolysis

Na-deposited TiO 2 nanotubes for photo electrochemical water splitting with enhanced activity – A novel approach

Mn/Fe co-doped TiO 2 nanotube arrays for photoelectrochemical water splitting in neutral medium

Titanium Doped Nanoporous Hematite Photoanode Modified with NiFeCoAlOOH Nanoparticles for Efficient Photoelectrochemical Water Splitting

Photoelectrochemical performance of TiO2 nanotube arrays modified with Ni2P Co-catalyst

Facile Fabrication of Organic/inorganic Nanotube Heterojunction Arrays for Enhanced Photoelectrochemical Water Splitting.

NaBH4 Reduction of TiSiO Nanotubes Photoanode for High-Efficiency Photoelectrochemical Water Splitting

Black Si-doped TiO2 Nanotube Photoanode for High-Efficiency Photoelectrochemical Water Splitting

Au nanostructure-decorated TiO2 nanowires exhibiting photoactivity across entire UV-visible region for photoelectrochemical water splitting.

Invited) Doped Titania Oxide Nanotubes for Photoelectochemical Water Splitting

Fabrication of MnO2/TiO2 nano-tube arrays photoelectrode and its enhanced visible light photoelectrocatalytic performance and mechanism

Facile Fabrication of Si-doped TiO2 Nanotubes Photoanode for Enhanced Photoelectrochemical Hydrogen Generation

Electrochemically Induced Ti3+ Self-Doping of TiO2 Nanotube Arrays for Improved Photoelectrochemical Water Splitting

Ultra-thin carbon doped TiO2 nanotube arrays for enhanced visible-light photoelectrochemical water splitting