Abstract:<p>Fluorinated polyhedral oligomeric silsesquioxane (F-POSS) is one of the most popular candidates at present for superhydrophobic coating. Because of its ultralow surface energy, F-POSS has usually been dissolved with expensive fluoro-solvents, and the melting temperature of F-POSS is not high (122–140 °C), which will cause its loss during use. So trying to polymerize/crosslink F-POSS molecules and/or directly graft F-POSS to substrate is important. In this work, we report the SI-eATRP grafting of methacryl POSS (MA-POSS) on cotton and the subsequent amine catalyzed thiol-methacrylate Michael addition reaction of poly(MA-POSS) with 1H, 1H, 2H, 2H-perfluorododecyl-1-thiol (PFDT) for the fabrication of a durable poly(MA-POSS)-PFDT coating. The cotton fabric coated with poly(MA-POSS) was nearly superhydrophobic after 4 h of SI-eATRP process under potentiostatic condition of −0.40 V. Although the water contact angle (WCA) was ~148°, water droplets tended to adhere to the cotton fabric surface even when the fabric was turned upside down. After fluorination, WCA was increased to ~160°, and water drops could slide off when the fabric was slightly tilted. The sliding angle (SA) was ~10°. The as-prepared poly(MA-POSS)-PFDT coating was durable against repeated washing and physical abrasion. After 30 accelerated washing cycles (equals to 150 home laundering cycles), the coated fabric still showed superhydrophobicity. After 800 abrasion cycles over sandpaper, the WCA was still as high as 149°. In addition, the coated fabric had self-healing ability and could restore its superhydrophobicity after plasma etching through heat treatment. After 10 cycles of plasma etching and heat-induced healing process, the WCA of the coated fabric kept at ~154°. Such a durable superhydrophobic fabric coating may find applications in the development of functional clothing for a variety of purposes.</p>

Superhydrophobic cotton fabrics: a quick and easy method of modification

Transformation of Hydrophilic Cotton Fabrics into Superhydrophobic Surfaces for Oil/water Separation

Durable, highly hydrophobic modification of cotton fabric with fluorine-free polysiloxanes obtained via hydrosilylation and hydrothiolation reactions

Study on simple preparation technique of superhydrophobic cotton fabrics

Preparation and properties of super hydrophobic cotton fabric constructed by modified nano-SiO 2 hybrid fluoro-epoxy copolymer

Functional Silane-Based Nanohybrid Materials for the Development of Hydrophobic and Water-Based Stain Resistant Cotton Fabrics Coatings

Thiol-ene chemistry as an effective tool for hydrophobization of cotton fabrics

Surface Modification of Polyester/Viscose Fabric with Silica Hydrosol and Amino-Functionalized Polydimethylsiloxane for the Preparation of a Fluorine-Free Superhydrophobic and Breathable Textile

A facile approach for fabricating fluorine-free superhydrophobic cotton fabric and its self-cleaning property

Nanoparticle-free, Fluorine-free, and Robust Superhydrophobic Cotton Fabric Fabricated Using a Combination of Etching Method and Mist Polymerization Technology

Synthesis of Fluoro-Containing Superhydrophobic Cotton Fabric with Washing Resistant Property Using Nano-Sio(2) Sol-Gel Method

Fabrication Of Superhydrophobic Cotton Fabrics Through Wrapping Silica With Plasma-Induced Grafting Polymerization

Super-Hydrophobicity of Polyester Fabrics Driven by Functional Sustainable Fluorine-Free Silane-Based Coatings

Synthesis of polysiloxane and its co-application with nano-SiO2 for antibacterial and hydrophobic cotton fabrics

Superhydrophobic and Photocatalytic Self-Cleaning Cotton Fabrics Coated with SiO2–TiO2 Janus Particles and PDMS

Durable superhydrophobic cotton fabrics prepared by surface-initiated electrochemically mediated ATRP of polyhedral vinylsilsesquioxane and subsequent fluorination via thiol-Michael addition reaction

Preparation of durable superamphiphobic cotton fabrics with self-cleaning and liquid repellency

THE STABILITY OF SUPERHYDROPHOBIC COTTON FABRICS PREPARED BY SOL–GEL COATING OF SiO2 AND TiO2

Robust superhydrophobic cotton fabrics based on nano-silica particles hybrid epoxy resin: self-cleaning, anti-fouling, anti-abrasion and oil–water separation

Fabrication of Superhydrophobic Fluorine-Free Films on Cotton Fabrics Through Plasma-Induced Grafting Polymerization of 1,3,5,7-Tetravinyl-1,3,5,7-tetramethylcyclotetrasiloxane

Rational design of multi-layered superhydrophobic coating on cotton fabrics for UV shielding, self-cleaning and oil-water separation