Abstract:Most of the super hydrophobic cotton fabric surfaces changed the original properties of cotton fabric and cannot be continuously used for oil-water separation. In this paper, the fluorine-containing epoxy polymer P(GMA- r -DFMA) was reacted with KH550 modified nano-SiO 2 to obtain an organic-inorganic hybrid super hydrophobic solution. By dipping process, the super hydrophobic cotton fabric surface was obtained. P(GMA- r -DFMA) can reduce the surface energy of cotton fabric, and modified silica can improve the surface roughness of cotton fabric to achieve super hydrophobic effect. The optimum parameters (polymer concentration, soaking time, drying time and drying temperature) for constructing super hydrophobic cotton fabric surface were explored. The optimal parameters are polymer concentration 5 mg/mL, soaking time 5 h, drying time 4 h, and drying temperature 120 °C. Under the optimal conditions, the water contact angle of the modified cotton fabric surface is 162 ± 3° and the water rolling angle is 10 ± 1°. The study on surface self-cleaning property of modified cotton fabric shows that modified cotton fabric can be restored to clean state after being soiled by toner and washed by deionized water. When the oils were n -hexane, n -octane and trichloromethane, the oil-water separation efficiency of the modified cotton fabric could reach 98 %, 98 % and 96 %, and the effect was stable. The surface of modified cotton fabric has obvious silver mirror phenomenon. The results of Scanning Electron Microscopy showed that the surface of cotton fabric was smooth before modification, but many small bumps and folds were added on the fabric surface after super hydrophobic modification, and the roughness became larger. The super hydrophobic coating is very thin and does not change the color, softness and other properties of the cotton fabric.

Fabrication Of Superhydrophobic Cotton Fabrics Through Wrapping Silica With Plasma-Induced Grafting Polymerization

Transformation of Hydrophilic Cotton Fabrics into Superhydrophobic Surfaces for Oil/water Separation

Study on simple preparation technique of superhydrophobic cotton fabrics

Fabrication of Superhydrophobic Fluorine-Free Films on Cotton Fabrics Through Plasma-Induced Grafting Polymerization of 1,3,5,7-Tetravinyl-1,3,5,7-tetramethylcyclotetrasiloxane

Preparation and properties of super hydrophobic cotton fabric constructed by modified nano-SiO 2 hybrid fluoro-epoxy copolymer

Nanoparticle-free, Fluorine-free, and Robust Superhydrophobic Cotton Fabric Fabricated Using a Combination of Etching Method and Mist Polymerization Technology

Hydrophobic modification of cotton fabric by helium low temperature plasma induced graft polymerization

Fabrication of Durable Superhydrophobic and Superoleophilic Cotton Fabric with Fluorinated Silica Sol Via Sol-Gel Process

Superhydrophobic cotton nonwoven fabrics through atmospheric plasma treatment for applications in self-cleaning and oil–water separation

Synthesis of Fluoro-Containing Superhydrophobic Cotton Fabric with Washing Resistant Property Using Nano-Sio(2) Sol-Gel Method

One-step Fabrication of Flexible, Durable and Fluorine-Free Superhydrophobic Cotton Fabrics for Efficient Oil/water Separation

Rational design of multi-layered superhydrophobic coating on cotton fabrics for UV shielding, self-cleaning and oil-water separation

Superhydrophobic Cotton Fabrics Prepared By Sol-Gel Coating Of Tio2 And Surface Hydrophobization

Fabrication of UV Curable Coating for Super Hydrophobic Cotton Fabrics

A facile approach for fabricating fluorine-free superhydrophobic cotton fabric and its self-cleaning property

Preparation of durable superamphiphobic cotton fabrics with self-cleaning and liquid repellency

One-pot Fabrication of Superhydrophobic and Flame-Retardant Coatings on Cotton Fabrics Via Sol-Gel Reaction.

Superhydrophobic and Photocatalytic Self-Cleaning Cotton Fabrics Coated with SiO2–TiO2 Janus Particles and PDMS

Antimicrobial Cotton Textiles with Robust Superhydrophobicity Via Plasma for Oily Water Separation

THE STABILITY OF SUPERHYDROPHOBIC COTTON FABRICS PREPARED BY SOL–GEL COATING OF SiO2 AND TiO2

Facile fabrication of superhydrophobic and flame-retardant coatings on cotton fabrics via layer-by-layer assembly