Abstract:Statement of problem The integration of computer-aided design and computer-aided manufacture (CAD-CAM) technology has revolutionized restorative dentistry, offering both additive and subtractive manufacturing methods. Despite extensive research on 3-dimensionally (3D) printed materials, uncertainties remain regarding the impact of print orientation on their mechanical properties, especially for definitive resin materials, necessitating further investigation to ensure clinical efficacy. Purpose The purpose of this in vitro study was to investigate the influence of print orientation and artificial aging on the flexural strength (FS) and flexural modulus (FM) of 3D printed resin materials indicated for definitive and interim restorations. Material and methods Specimens (2×2×25 mm) were additively manufactured in 3 orientations (0, 45, and 90 degrees) using five 3D printed resins: VarseoSmile Crownplus (VCP), Crowntec (CT), Nextdent C&B MFH (ND), Dima C&B temp (DT), and GC temp print (GC). A DLP 3D printer (ASIGA MAX UV) was used with postprocessing parameters as per the manufacturer recommendations. FS and FM were tested after storage in distilled water (DW) and artificial saliva (AS) for 24 hours, 1 month, and 3 months at 37 °C. Additional 2×2×16-mm specimens printed at 90 degrees were compared with the milled materials Lava Ultimate (LU) and Telio CAD (TC) after 24 hours of storage in AS at 37 °C (n=10). Measurements were conducted using a universal testing machine (Z020; Zwick/Roell) following the International Organization for Standardization (ISO) 4049 standard. Multiple way ANOVA, 1-way ANOVA, and Tukey HSD post hoc tests (α=.05) were used to analyze the data. Results Print orientation significantly influenced the FS and FM of 3D printed resin materials, with the 90-degree orientation exhibiting superior mechanical properties ( P <.05). Definitive resins (CT and VCP) exhibited higher FS and FM compared with interim resins (ND, DT, GC) at all time points ( P <.001). LU had significantly higher FS and FM compared with other resins ( P <.001), while TC had similar FS to definitive 3D printed resins. Aging time and media influenced FS and FM, with varying effects observed across different materials and time points. Strong positive correlations were found between filler weight and both FS (r=.83, P =.019) and FM. All materials met the minimum FS requirement of 80 MPa (ISO 4049) when printed at 90 degrees. Conclusions The 90-degree orientation produced specimens with higher FS than 0- and 45-degree orientations. CT recommended for definitive restorations displayed higher FS compared with VCP and those intended for interim use after 3 months of aging. LU exhibited higher FS and FM than 3D printed resins, while TC had similar FS and FM to the latter. Aging effects on 3D printed resins were minimal and were material specific.

Effect of thermal cycling on the flexural strength of 3-D printed, CAD/CAM milled and heat-polymerized denture base materials

Effect of thermal cycling on the flexure strength of CAD-CAM denture base materials: An in vitro study

Effect of thermocycling on the mechanical properties of permanent composite-based CAD-CAM restorative materials produced by additive and subtractive manufacturing techniques

Evaluation of the effect of thermocycling on the trueness and precision of digitally fabricated complete denture bases

Effect of thermocycling on tensile bond strength of autopolymerized, heat-polymerized, milled, and 3D printed denture base materials bonded to 4 different denture liners: an in vitro study

A comparison of the mechanical properties of 3D-printed, milled, and conventional denture base resin materials

Effect of thermocycling on surface topography and fracture toughness of milled and additively manufactured denture base materials: an in-vitro study

Flexural Strength Analysis of Different Complete Denture Resin-Based Materials Obtained by Conventional and Digital Manufacturing

Postpolymerization of a 3D-printed denture base polymer: Impact of post-curing methods on surface characteristics, flexural strength, and cytotoxicity

Assessing the physical and mechanical properties of 3D printed acrylic material for denture base application

In vitro evaluation of the mechanical and optical properties of 3D printed vs CAD/CAM milled denture teeth materials

Influence of CAD/CAM Milling and 3D-Printing Fabrication Methods on the Mechanical Properties of 3-Unit Interim Fixed Dental Prosthesis after Thermo-Mechanical Aging Process

Effects of print orientation and artificial aging on the flexural strength and flexural modulus of 3D printed restorative resin materials

The effect of various surface treatments on the repair bond strength of denture bases produced by digital and conventional methods

Effect of aging on dimensional accuracy and color stability of CAD-CAM milled and 3D-printed denture base resins: a comparative in-vitro study

Effect of Aging on the Mechanical Properties of CAD/CAM–Milled and 3D-Printed Acrylic Resins for Denture Bases

Repair strength of 3D‐printed denture base resins: Effect of surface treatment and repair material type

Flexural strength, fracture toughness, translucency, stain resistance, and water sorption of 3D‐printed, milled, and conventional denture base materials

Effect of artificial aging and different surface finishing protocols on the flexural strength and surface hardness of a photopolymer for manufacturing monolithic polychromatic complete dentures using PolyJet 3D printing

Influence of the Printing Angle and Load Direction on Flexure Strength in 3D Printed Materials for Provisional Dental Restorations

Flexural strength, surface roughness, micro-CT analysis, and microbiological adhesion of a 3D-printed temporary crown material