Passivation and corrosion of Al current collectors in lithium-ion batteries

Pin Du,Jiale Wan,Jiakang Qu,Hongwei Xie,Dihua Wang,Huayi Yin

DOI: https://doi.org/10.1038/s41529-024-00453-x

2024-04-26

npj Materials Degradation

Abstract:State-of-the-art lithium-ion batteries inevitably suffer from electrode corrosion over long-term operation, such as corrosion of Al current collectors. However, the understanding of Al corrosion and its impacts on the battery performances have not been evaluated in detail. The passivation, its breakdown, and corrosion of the Al resulted in the deterioration of the solid/solid interface and electrode integrity. Additionally, localized diffusion of F − /Al 3+ brought the irreversible current detrimental to the Coulomb efficiency (1.14% loss). Eventually, the behavior led to extensive capacity damage (>20%) to battery performance until lifespan. During the battery cycling, the passivation layer greater than 20 nm was generated near the median voltage. When the charging voltage rose, the passivation layer was squeezed and deformed by the newly generated Al-F-O particles, resulting in stress corrosion cracks. The passivation layer peeled off, and the nano-passivation layer material was re-generated as the voltage continued to rise. The above results were repeated, and the Al matrix was continuously consumed. The passivity breakdown with localized corrosion was derived from ethylene carbonate adsorption, which was highly correlated to the charge voltages, especially at 4.4 V and 4.8 V. The results will serve as a benchmark for electrode corrosion of other advanced energy storage materials, which is crucial for electrode engineering and performance modulation using interfacial design.

materials science, multidisciplinary

What problem does this paper attempt to address?

The problems that this paper attempts to solve are the passivation, passivation layer rupture and corrosion of the aluminum current collector in lithium - ion batteries, which have a significant impact on battery performance. Specifically:

1. **Electrode corrosion and its impact on battery performance**: High - performance lithium - ion batteries will inevitably suffer from electrode corrosion during long - term operation, especially the corrosion of the aluminum current collector. However, the aluminum corrosion and its impact on battery performance have not been evaluated in detail yet. The passivation, passivation layer rupture and corrosion of aluminum lead to the deterioration of the solid - solid interface and electrode integrity.

2. **Changes in the passivation layer and local diffusion**: When the passivation layer thickness exceeds 20 nanometers, it is generated near the median voltage. When the charging voltage increases, the newly generated Al - F - O particles squeeze and deform the passivation layer, resulting in stress - corrosion cracks. As the voltage continues to rise, the passivation layer peels off and regenerates nano - passivation layer materials, resulting in continuous consumption of the aluminum substrate.

3. **Local diffusion of fluoride ions and aluminum ions**: The local diffusion of F⁻/Al³⁺ brings about irreversible current loss (Coulomb efficiency loss of 1.14%), and finally leads to extensive capacity damage (> 20%) of battery performance until the end of its life.

4. **Impact of electrolyte components**: The passivation layer rupture induced by ethylene carbonate adsorption is closely related to the charging voltage, especially at 4.4 V and 4.8 V. These results provide a benchmark for electrode corrosion of other advanced energy - storage materials, which is crucial for electrode engineering and performance regulation.

5. **Stability at high voltages**: In order to achieve lithium - ion batteries with higher energy density, it is necessary to improve their structural stability and stability at high cut - off voltages. Therefore, it is very urgent to study the corrosion behavior of the aluminum current collector at different voltages and its impact on battery performance.

Through the above research, the author aims to reveal the corrosion mechanism of the aluminum current collector in lithium - ion batteries and its impact on battery performance, which is of great significance for understanding the stability of the aluminum current collector in various energy - storage materials at high voltages.

### Formula summary

1. Reaction between aluminum oxide and hydrofluoric acid:
\[
\text{Al}_2\text{O}_3+6\text{HF} = 2\text{AlF}_3+3\text{H}_2\text{O}
\]

2. Anodic dissolution reaction of aluminum:
\[
\text{Anode: Al}-3e^-\rightarrow\text{Al}^{3 +}
\]

3. Calculation of microstructure volume expansion:
\[
\frac{2\times\text{Molar volume}(\text{AlF}_3/C0)}{\text{Molar volume}(\text{Al}_2\text{O}_3)}\times100\% = 64\%
\]

These formulas and contents show the chemical reactions and physical changes of the aluminum current collector under different conditions, which help to understand its corrosion mechanism in lithium - ion batteries.