Abstract:A newly developed method for the formation of nanowires by self-aggregation of nanoparticles is presented in this paper. Co3C, Co-rich, and Ni nanoparticles dispersed on holey carbon grids are inserted in a vacuum oven and are co-annealed with PolyChloroTriFluoroEthylene (PCTFE) at 375 degrees C. No external electric or magnetic fields were applied. High resolution electron microscopy (HREM) was extensively used to determine the shape, size distribution and crystallographic phase of the starting and produced materials. Interestingly, after an annealing circle of 72 hours, the nanoparticles seem to self-agglomerate into nanowires which have diameters in the 5-20 nm range and lengths exceeding at cases 1 micron. The diameter of the produced wires is in the same range as the diameter of the initial nanoparticles, further supporting the notion that the nanowires have formed out of nanoparticle agglomeration. Close inspection of nanowire HREM images shows that the core structure of nanowires wider than approximately 11 nm resembles linked nanoparticles. Phase identification performed using the HREM images reveals the core is of the same phase/material as the starting nanoparticles. Since nanowires appear to form over holes on the holey carbon grid, a base growth mechanism is proposed. The fluorocarbon vapour decomposes over the transitional metal nanoparticles and carbon tubules start growing. The nanoparticles appear to be trapped inside the tubules where their close proximity enhances their fusion into a continuous core. At the studied temperature, the nanoparticle fusion is seen to be limited by the size of the nanoparticles manifested by continuous cores only in the thin nanowires. The process presented here shows that nanoparticles can spontaneously self-align into nanowires in a way and to an extent never reported before. Therefore there is certainly scope for studying this method further to reveal more information about the catalytic action of transitional metals on hydrocarbons and the exact nanowire formation mechanism. Although it is currently a matter of speculation, this process might lead to the effortless growth of nanowires at particular places when building miniature circuits.

Nucleation and Growth Mechanisms of Bimetallic Sm-Co Nanowires and Nanotubes

On the Growth Mechanism of Nickel and Cobalt Nanowires and Comparison of Their Magnetic Properties

Spontaneous self-agglomeration of magnetic nanoparticles into nanowires

Growth and Nanoscale Magnetic Properties of Ferromagnetic Nanowire Encapsulated Inside Carbon Nanotubes

Growth Orientation Control of Co Nanowires Fabricated by Electrochemical Deposition Using Porous Alumina Templates

Initial Growth of Single-Crystalline Nanowires: from 3D Nucleation to 2D Growth.

Growth Kinetics of Nickel Crystals in Nanopores

Interface catalytic reduction of alumina by nickle for the aluminum nanowire growth: Dynamics observed by in situ TEM

A two-stage mechanism of bimetallic catalyzed growth of single-walled carbon nanotubes

Growth of single-crystalline Co 7 Fe 3 nanowires via electrochemical deposition and their magnetic properties

Magnetic Properties of Ferromagnetic Nanowires Embedded in Nanoporous Alumina Membranes

Experimental investigations and micromagnetic simulations of hybrid CoCr2O4/Ni coaxial nanostructures.

Magnetic properties of Co–Pt alloy nanowire arrays in anodic alumina templates

Manipulation of Morphology and Magnetic Properties in Cobalt Nanowires

Crystal growth and magnetic reversal mechanism in ferromagnetic nanowire by chain of prolate spheroids model

Template Synthesis and Growth Mechanism of Metal Nanowire/carbon Nanotube Heterojunctions.

Electrodeposition of Ni and Ni-Cu Nanowires in Rectified Porous Anodic Alumina Membrane

Synthesis, Characterization, and Formation Mechanism of Crystalline Cu and Ni Metallic Nanowires under Ambient, Seedless, Surfactantless Conditions

A preliminary study on the synthesis and characterization of multilayered Ag/Co magnetic nanowires fabricated via the electrodeposition method

Highly Efficient Direct Electrodeposition of Co−Cu Alloy Nanotubes in an Anodic Alumina Template