Abstract:The high activity and stability of intermetallic PtCo nanocatalysts toward oxygen reduction reaction make them a top candidate as low-Pt cathode catalysts in proton exchange membrane fuel cells (PEMFCs). However, forming intermetallic structures typically requires high-temperature annealing, posing a challenge for achieving well-size control and highly ordered structures. Here we report the design and synthesis of bimetallic core@shell structured precursors for affording high-performance intermetallic PtCo catalysts. The fabrication of the core@shell precursor involves using a molecular ligand containing both sulfur and oxygen donors to selectively bind with Pt colloidal nanoparticles as the core and chelate Co ions as the shell. During high-temperature annealing, the ligand transforms into carbon coatings around alloy nanoparticles, preventing particle sintering; meanwhile, Co ions in the shell can easily diffuse into the Pt core, which helps to increase the thermodynamic driving force for forming intermetallic structures. These benefits enable us to obtain the catalyst with finely dispersed nanoparticles (similar to 3.5 nm) and a high ordering degree of 72%. With 0.1 mgPt/cm(2) cathode loading, the catalyst delivers superior performance and durability in PEMFCs, showing an initial mass activity of 0.56 A/mgPt, an initial power density of 1.05 W/cm(2) at 0.67 V (H2-air), and a voltage loss of 26 mV at 0.8 A/cm(2) after the accelerated durability test. (c) 2024 Science Press and Dalian Institute of Chemical Physics, Chinese Academy of Sciences. Published by Elsevier B.V. and Science Press. All rights are reserved, including those for text and data mining, AI training, and similar technologies.

Co dendrite based bimetallic structures with nanoflake-built Pt covers and strong catalytic activity.

Enhancing the Catalytic and Electrocatalytic Properties of Pt-based Catalysts by Forming Bimetallic Nanocrystals with Pd

Formation of PtCuCo Trimetallic Nanostructures with Enhanced Catalytic and Enzyme-like Activities for Biodetection

Single-Crystalline Dendritic Bimetallic And Multimetallic Nanocubes

Epitaxial Growth of Multimetallic Pd@PtM (M = Ni, Rh, Ru) Core-Shell Nanoplates Realized by in Situ-Produced CO from Interfacial Catalytic Reactions.

Synthesis of PtCo 3 polyhedral nanoparticles and evolution to Pt 3 Co nanoframes

Concentration-dependent Morphology Control of Pt-coated-Ag Nanowires and Effects of Bimetallic Interfaces on Catalytic Activity

Synthesis of Pd-Pt Bimetallic Nanocrystals with a Concave Structure Through a Bromide-Induced Galvanic Replacement Reaction.

A general strategy for bimetallic Pt-based nano-branched structures as highly active and stable oxygen reduction and methanol oxidation bifunctional catalysts

Bimetallic Synergy from a Reaction-Driven Metal Oxide–Metal Interface of Pt–Co Bimetallic Nanoparticles

Efficient Synthesis Of Bimetallic Pt3zn Alloy Nanocrystals With Different Shapes And Their Enhanced Electrocatalytic Activity

Synergistic Bimetallic Metallic Organic Framework-Derived Pt-Co Oxygen Reduction Electrocatalysts

Morphology and Phase Controlled Construction of Pt-Ni Nanostructures for Efficient Electrocatalysis.

Intermetallic hcp-PtBi/fcc-Pt Core/Shell Nanoplates Enable Efficient Bifunctional Oxygen Reduction and Methanol Oxidation Electrocatalysis

Direct Growth of Uniform Bimetallic Core‐Shell or Intermetallic Nanoparticles on Carbon via a Surface‐Confinement Strategy for Electrochemical Hydrogen Evolution Reaction

Pt-M (M = Cu, Fe, Zn, Etc.) Bimetallic Nanomaterials with Abundant Surface Defects and Robust Catalytic Properties

Bimetallic and Postsynthetically Alloyed PtCu Nanostructures with Tunable Reactivity for the Methanol Oxidation Reaction

Synthesis of Intermetallic PtCo Fuel Cell Catalysts from Bimetallic Core@shell Structured Nanoparticles

Atomic Structure Evolution of Pt–Co Binary Catalysts: Single Metal Sites versus Intermetallic Nanocrystals

One-Pot Protocol for Bimetallic Pt/Cu Hexapod Concave Nanocrystals with Enhanced Electrocatalytic Activity

Ag Dendrite-Based Au/Ag Bimetallic Nanostructures with Strongly Enhanced Catalytic Activity.