Enhanced performance of solution-processed all-inorganic halide perovskite photodetectors by using bulk heterojunction and lateral configuration

Peiyun Tang,Shengyi Yang,Jinming Hu,Zhenheng Zhang,Yurong Jiang,Muhammad Sulaman,Libin Tang,Bingsuo Zou

DOI: https://doi.org/10.1016/j.jallcom.2021.163022

IF: 6.2

2022-03-01

Journal of Alloys and Compounds

Abstract:Currently, all-inorganic halide perovskites are widely investigated for their applications in optoelectronics due to their excellent physical and chemical properties. In this paper, solution-processed bulk-heterojunction lateral photodetectors Ag/CsPbBr3:ZnO/Ag were built to enhance device performance, in which the active CsPbBr3 layer were surface-passivated by ZnO nanoparticles (NPs) in an optimized molar ratio. By optimizing the molar ratio of CsPbBr3 to ZnO NPs (i.e. k R =M CsPbBr3/M ZnO), the photocurrent from the lateral photodetector was greatly enhanced and, the dark current was suppressed to as low as 10−12 A due to the lateral configuration by employing a 50 µm-width active layer made through an interdigital mask. As a result, the On/Off current ratio of the lateral photodetector Ag/CsPbBr3:ZnO/Ag reaches to more than 103 for an optimum molar ratio k R = 1:1, and it is 300-folds higher than that of the control device Ag/CsPbBr3/Ag, showing a maximum specific detectivity D* of 1.6 × 1011 Jones with a photoresponsivity of 3.8 mA/W under 16 µW/cm2 405 nm illumination at − 5 V. In this way, it provides an efficient method for solution-processed high-performance photodetectors by combining bulk heterojunction and lateral configuration.

materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering