Abstract:Highlights • The WAAM-processed AZ31 block exhibits a fully equiaxed grain morphology. • The Al 8 Mn 5 in the AZ31 block acts as the heterogeneous nucleation core of Mg 17 Al 12 . • The electromagnetic stirring effect during the WAAM process can effectively refine the microstructure of the AZ31 alloy. • The top of the AZ31 block has the best strength and elongation matching properties. • The influence of fine crystals on the strength of AZ31 is much larger than that of the precipitation strengthening effect. With the urgent demand for lightweight and integrated structural parts in the aerospace field, the use of cold metal transfer wire arc additive manufacturing (CMT-WAAM) to form large-size magnesium alloy structural parts has become a research hotspot. In this paper, a large AZ31 magnesium alloy multilayer block with a lower porosity was successfully prepared by CMT-WAAM. The AZ31 block exhibits a fully equiaxed grain morphology, the average grain diameters of the top, middle, and bottom are 16.1 μm, 12.4 μm, and 10.4 μm, respectively. The submicron spherical particles measuring 0.09 to 0.4 μm are Mg 17 Al 12 phases, irregular particles are Al 8 Mn 5 + Mg 17 Al 12 composite phases and large particles measuring 5 to 10 μm are Al 8 Mn 5 in AZ31 block. The UTS of CMT-WAAM AZ31 block from the bottom of 239.9 ± 5.0 MPa to the top of 237.3 ± 3.1 MPa, and the EL from the bottom of 22.7 ± 0.6 % to the top of 30.0 ± 1.1 %, exceeding the casting standards. In the CMT-WAAM processed AZ31 alloy, the pre-existing coarse second phase particles in the AZ31 filaments acted as nucleating agents, and the electromagnetic stirring effect in the WAAM process broke up the dendrites and increased the number density of nucleation sites to improve the rate of nucleation, and the complex thermal conditions in the WAAM process restricted the growth of the grains and the precipitated phases. The mechanical properties of AZ31 alloy were improved by effectively refining its grain size and precipitated phase size.

Study on anisotropy of microstructure and mechanical properties of AZ31 magnesium alloy fabricated by wire arc additive manufacturing

Microstructure and mechanical properties of AZ31 magnesium alloy prepared using wire arc additive manufacturing

Microstructure and mechanical properties of wire and arc additive manufactured AZ31 magnesium alloy using cold metal transfer process

Wire arc additive manufacturing of a novel ATZM31 Mg alloy: Microstructure evolution and mechanical properties

Mechanical Properties, Microstructural Characteristics and Heat Treatment Effects of WAAM Stainless-Steel Plate Material

Wire-arc additive manufacturing of AZ31 magnesium alloy fabricated by cold metal transfer heat source: Processing, microstructure, and mechanical behavior

Additive manufacturing of high performance AZ31 magnesium alloy with full equiaxed grains: Microstructure, mechanical property, and electromechanical corrosion performance

Achieving equiaxed microstructure and isotropic mechanical properties of additively manufactured AZ31 magnesium alloy via ultrasonic frequency pulsed arc

Microstructure evolution and mechanical properties of large-size AZ31 magnesium alloy block fabricated by wire arc additive manufacturing

Microstructures and Mechanical Properties of Al–Zn–Mg Aluminium Alloy Samples Produced by Wire + Arc Additive Manufacturing

Tensile, Fatigue Properties and Their Anisotropies of Al-Mg Alloy Fabricated by Wire-Arc Additive Manufacturing

Formability, microstructure evolution and mechanical properties of wire arc additively manufactured AZ80M magnesium alloy using gas tungsten arc welding

Microstructure and mechanical properties of WE43 magnesium alloy fabricated by wire-arc additive manufacturing

Effect of fabrication parameters on the microstructure and mechanical properties of wire arc additive manufactured AZ61 alloy

Inhomogeneity and anisotropy of Al-Zn-Mg-Cu alloy manufactured by wire arc additive manufacturing: microstructure, mechanical properties, stress corrosion cracking susceptibility

Microstructural Evolution and Strengthening Mechanism of Low Re-Content Mg-Zn-Re-Zr Alloy Fabricated by Wire Arc Additive Manufacturing

Microstructure and Mechanical Properties of Weaving Wire and Arc Additive Manufactured AZ91 Magnesium Alloy Based on Cold Metal Transfer Technique

On the fabrication of finer grain structure through using finer wire diameter for wire arc additive manufacturing of AZ31B magnesium alloy

Microstructure and mechanical properties of GTA-based wire arc additive manufactured AZ91D magnesium alloy

Wire arc additive manufacturing of Al-Zn-Mg-Cu alloy: Microstructures and mechanical properties

Microstructure and mechanical properties of Mg-Gd-Y-Zn-Zr alloy fabricated by cold metal transfer wire arc additive manufacturing