Abstract:Because of their low density, high strength-to-weight ratio and high damping capacity, magnesium alloys have gained increasing applications in many fields, especially for die-cast magnesium alloys. The application of die-cast magnesium alloys in structures and repair welding of casting defects necessitates the development of welding techniques. As a high energy density thermal source, laser welding can reduce many welding defects compared with conventional welding methods, but pore formation during welding of die-cast magnesium alloys is still a severe problem that has not been solved. This paper seeks to identify the mechanism of pore formation during laser welding of die-cast magensium alloys and search for a metallurgic solution of porosity. The great tendency to pore formation in die-cast magnesium alloys is attributed to high gas content in the base metal. The characteristic of gas source in die-cast magnesium alloys and the process of pore formation during laser welding are studied by some experiments including analysis of characteristic parameters of pores (porosity, average diameter and number densities), change of densities before and after heating (350 degrees C, holding time 1 h) and pore formation tendency under different vacuo heating conditions (heating the base metal to 350 degrees C under vacuum environment of different holding time). The results show that heating increases porosity, average diameter and number densities, which lead to the reduction of bulk density. Vacuo heating before welding can reduce porosity to a great extent, and with holding time prolonging, porosity reduces. In die casting, there are molecular hydrogen and atomic hydrogen in die-cast magnesium alloys. The hydrogen gas (molecular hydrogen) in high pressure pores in the base metal expands sharply in the molten pool, and the oversaturated atomic hydrogen can also form new pores or contribute to the growth of exsisting pores. That is to say that both molecular hydrogen and atomic hydrogen contribute to the pore formation of die-cast magnesium alloys during laser welding. During vacuo heating before welding, atomic hydrogen can escape in part through diffusion, thus reducing the tendency to form pores. With holding time of vacuo heating prolonging, the amount of atomic hydrogen escaping from the base metal increases, thus porosity reduces. Adding elements, which can combine hydrogen to form hydride, may be a possible solution to pore formation in die-cast magnesium alloys. Preliminary experiments show that adding Zr to welds during welding can reduce the tendency to form pores obviously, the reason for this needs further research.

A porous magnesium alloy preparation method

Method for processing magnesium alloy

Magnesium alloy and preparation method thereof

Preparation method for rare earth-magnesium alloy

Deforming magnesium alloy and preparation method thereof

Preparation, Characterization and Designing of Porous Ti–6Al–4V Through Metal Injection Molding Without Space Holder

A novel porous magnesium production through powder metallurgy technique using wire-pieces of titanium space holder for bone scaffold materials

Novel Efficient Reduction Route for Magnesium Production Using Silicothermic Process

Mechanisms for the Formation of Porous Micro-Arc Oxidation Coatings on Magnesium Alloys

EXPERIMENTAL STUDY ON THE REASON OF PORE FORMATION IN LASER WELDING OF DIE-CAST MAGNESIUM ALLOY

Manufacturing of porous magnesium scaffolds for bone tissue engineering by 3D gel-printing

Mechanical and corrosion performance of Mg alloy via 3DP by full liquid phase sintering

Process for preparing pretreatment layer and coating on magnesium and magnesium alloy surface

Highly Porous Magnesium Alloy Structures and Their Properties Regarding Degradable Implant Application

Preparation of high purity magnesium by vacuum gasification-directional condensation technology

Additive manufacturing of magnesium–zinc–zirconium (ZK) alloys via capillary-mediated binderless three-dimensional printing

Preparation and Performance of the Magnesium Matrix Composite Reinforced with Al2O3-SiO2 Short Fibers

Experimental Study of Magnesium (Mg) Production by an Integrated Calcination and Silicothermic Reduction Short Process

Towards additive manufacturing of magnesium alloys through integration of binderless 3D printing and rapid microwave sintering

Bidirectional Solidification of Radial-Type Porous Magnesium

Preparation and properties of porous MgO based ceramics from magnesite tailings and fused magnesia