Abstract:In this work, Cu-1.4 wt%Ta-Zr alloys with different Zr content (0, 0.1, 0.2 and 0.5 wt%) were fabricated by mechanical alloying combined with spark plasm sintering. The effect of Zr addition on the microstructures, mechanical properties and thermal stability of Cu-Ta alloy were characterized. Cu-Ta alloys composes of ultrafine equiaxed grains along with the uniformly dispersion of semi-coherent Ta nanoclusters and incoherent Ta coarse particles. As Zr is introduced into Cu-Ta alloy, the Ta precipitates were effectively refined, especially for the reduction of Ta coarse particles. The significant refinement effect of the grains is realized when Zr content reaches 0.2 wt%, and high-proportioned nano-sized grains are facilitated to form, along with the activation of a lot of twins and the formation of intermetallic composed of Cu and Zr. The dislocation density and strength increase remarkably with the increase of Zr content, and the highest strength (499 MPa for yield strength and 600 MPa for ultimate tensile strength) is achieved as the Zr content is up to 0.2 wt%. Compared with Cu-Ta alloy (382 MPa for yield strength and 560 MPa for ultimate tensile strength), the significant increment of 31% for the yield strength is successfully realized by Cu-Ta-0.2 wt%Zr alloy. Cu-Ta-0.2 wt%Zr alloys exhibit the excellent thermal stability, and the hardness keeps stable even the sample was annealed at 700 °C for 300 h, showing superior microstructural stability in comparison with Cu-Ta alloy (~4.5% reduction of the hardness after 300 h at 700 °C). The softening temperature of Cu-Ta-0.2 wt%Zr alloy is up to 1028 °C (1022 °C for Cu-Ta alloy) along with higher hardness than that of Cu-Ta alloy at the same annealing temperature. This study provides a new way to fabricate dispersion strengthened Cu alloys with high strength, exceptional thermal stability and softening resistance, which have great potential application value in the field of future fusion reactor.

Strengthening of Ta-W alloys by alloying Zr elements: First-principles calculation and experimental perspective

Effects of Zr Addition on the Deformation Behavior, Microstructure and Mechanical Properties of Dental Ti Alloys

Effects of Zr addition on the microstructures, mechanical properties and thermal stability of Cu-Ta alloys

Alloying Effects of Zr, Nb, Ta, and W on Thermodynamic and Mechanical Properties of TiC Based on First-Principles Calculation

Effect of Zr addition on the local structure and mechanical properties of Ti–Ta–Nb–Zr refractory high-entropy alloys

First-Principles Study of Structural Stability and Mechanical Properties of Ta–W–Hf Alloys

Effect of Ti Addition on the Microstructure and Mechanical Properties of Cast Mg-Gd-Y-Zn Alloys

Effect of tantalum concentration on the microstructure and mechanical properties of novel W–Ta-Re alloy

Ta W Refractory Alloys with High Strength at 2000C

Effect of different crystal forms of ZrO 2 on the microstructure and properties of tungsten alloys

Improved mechanical properties of W-Zr-Ti-Nb alloys via adding Ti and Nb

Effect of Ta on the microstructure and mechanical properties of W Ta alloys prepared by arc melting

Influence of Zr on grain orientation, texture, and mechanical properties in hot- and warm-rolled FeCrAl alloys

Influence of Oxygen and Zirconium Contents on The Mechanical Properties of Ti-23Nb-0.7Ta-Zr-O Alloys

Influence of Nb, Ta and Zr on the Interdiffusion Coefficients and Solid Solution Strengthening of γ-TiAl Single Phase Alloys

Effect of Ti on the Structure and Mechanical Properties of TixZr2.5-xTa Alloys.

Solving Strength–Toughness Dilemma in Superhard Transition-Metal Diborides via a Distinct Chemically Tuned Solid Solution Approach

Enhancement of tensile properties of Ti2AlNb alloy added with Ta element

Toughness Improvement By Zr Addition In The Simulated Coarse-Grained Heat-Affected Zone Of High-Strength Low-Alloy Steels

Synthesis and Mechanical Properties of Zr-Cu-Ni-Ta-Al Bulk Amorphous Alloy Matrix Composites

Extremely uniform nanosized oxide particles dispersion strengthened tungsten alloy with high tensile and compressive strengths fabricated involving liquid-liquid method