Abstract:<p>Impact damage are critical for damage tolerance assessment of high-speed train axles. Flying ballast impact damage on railway axles produces geometry discontinuities, which become preferential sites for fatigue crack initiation and usually lead to premature failure. According to this, the formation of surface impact damage and its influence on structural integrity of induction hardened S38C axles are herein explored. In particular, the morphology of impact damage on induction hardened S38C axles were analyzed as well as fatigue properties of specimens with artificial defects, electronic discharge machine (EDM) defects and impact defects fabricated by shooting metallic balls to the surface with compressive-gas gun. Results show that surface impact damage of the axles include two types, namely scratches and notches. Fatigue strength of the specimens with EDM defects are larger than the Murakami's model predictions due to existence of compressive residual stresses. The influence of shallower impact damage (less than 200μm) on the fatigue strength is negligible. With a larger depth, the rim is extracted out of the original surface and fatigue crack starts from this point with a decline of fatigue strength. Microcracks and loss of materials appear at the rim of impact damage, and microcracks along adiabatic shear bands lies beneath the surface when the impact depth is about 300μm resulting in 50% reduction of fatigue strength. Fatigue strengths of impacted specimens are larger than that of EDM specimens by 200MPa with the equivalent <span class="math"><math>area</math></span> due to the local residual stress.</p>

Overview of fatigue damage evaluation rule for railway axles in Japan and fatigue property of railway axle made of medium carbon steel

Determination of the critical defect and fatigue life of high-speed railway axles under variable amplitude loads

A New Approach for Studying Fatigue Damage

Fatigue resistance and remaining life assessment of induction-hardened S38C steel railway axles

Three-dimensional correlation of damage criticality with the defect size and lifetime of externally impacted 25CrMo4 steel

Fatigue strength evaluation of scale railway axle with surface defect considering mean stress effect

Fatigue Evaluation for High-Speed Railway Axles with Surface Scratch

Fatigue assessment of EA4T railway axles under artificial surface damage

Fatigue behaviour of EA4T notched specimens: Experiments and predictions using the theory of critical distance

Corrosion fatigue behaviors and life prediction of railway axle EA4T steel with artificial indentation

Fatigue life enhancement of foreign object impacted railway axle EA4T steel with surface shot peening

Foreign object damage tolerance and fatigue analysis of induction hardened S38C axles

Influence of artificial defects on fatigue strength of induction hardened S38C axles

Fatigue and damage tolerance assessment of induction hardened S38C axles under different foreign objects

Development of Fatigue Prediction System for Bogie Frame Using a Dynamic Analysis Model Based on High-Speed and High-Precision Stress Estimation Method

Experimental and numerical study on press-fitted railway axles: Competition between fretting and plain fatigue

Fatigue strength analysis of a welded railway vehicle structure by different methods

Fatigue Properties Improvement of Low-Carbon Alloy Axle Steel by Induction Hardening and Shot Peening: A Prospective Comparison

Gradient residual stress and fatigue life prediction of induction hardened carbon steel axles: Experiment and simulation

Fatigue life prediction of a railway hollow axle with a tapered bore surface

Study on fatigue damage tolerance of rail steel materials using peridynamics