Abstract:<p>Impact damage are critical for damage tolerance assessment of high-speed train axles. Flying ballast impact damage on railway axles produces geometry discontinuities, which become preferential sites for fatigue crack initiation and usually lead to premature failure. According to this, the formation of surface impact damage and its influence on structural integrity of induction hardened S38C axles are herein explored. In particular, the morphology of impact damage on induction hardened S38C axles were analyzed as well as fatigue properties of specimens with artificial defects, electronic discharge machine (EDM) defects and impact defects fabricated by shooting metallic balls to the surface with compressive-gas gun. Results show that surface impact damage of the axles include two types, namely scratches and notches. Fatigue strength of the specimens with EDM defects are larger than the Murakami's model predictions due to existence of compressive residual stresses. The influence of shallower impact damage (less than 200μm) on the fatigue strength is negligible. With a larger depth, the rim is extracted out of the original surface and fatigue crack starts from this point with a decline of fatigue strength. Microcracks and loss of materials appear at the rim of impact damage, and microcracks along adiabatic shear bands lies beneath the surface when the impact depth is about 300μm resulting in 50% reduction of fatigue strength. Fatigue strengths of impacted specimens are larger than that of EDM specimens by 200MPa with the equivalent <span class="math"><math>area</math></span> due to the local residual stress.</p>

Fatigue resistance and remaining life assessment of induction-hardened S38C steel railway axles

Gradient residual stress and fatigue life prediction of induction hardened carbon steel axles: Experiment and simulation

Corrosion fatigue behaviors and life prediction of railway axle EA4T steel with artificial indentation

Influence of artificial defects on fatigue strength of induction hardened S38C axles

Fatigue and damage tolerance assessment of induction hardened S38C axles under different foreign objects

Determination of the critical defect and fatigue life of high-speed railway axles under variable amplitude loads

Fatigue life enhancement of foreign object impacted railway axle EA4T steel with surface shot peening

Research on Size Effects in Fracture Properties and Residual Life Prediction for High-Speed Train Axles

Three-dimensional correlation of damage criticality with the defect size and lifetime of externally impacted 25CrMo4 steel

Foreign object damage tolerance and fatigue analysis of induction hardened S38C axles

Fatigue Properties Improvement of Low-Carbon Alloy Axle Steel by Induction Hardening and Shot Peening: A Prospective Comparison

Fatigue Evaluation for High-Speed Railway Axles with Surface Scratch

Experimental and numerical insights into fatigue crack propagation of railway component with gradient residual stress

Fatigue assessment of EA4T railway axles under artificial surface damage

Corrosion fatigue lifetime assessment of high-speed railway axle EA4T steel with artificial scratch

Numerical prediction of fretting fatigue crack growth in scaled railway axles considering fretting wear evolution

Study on fatigue damage tolerance of rail steel materials using peridynamics

A coupled wear and crack initiation-propagation methodology for fretting fatigue life assessment in press-fitted axles

Enhancement of Fatigue Endurance Limit through Ultrasonic Surface Rolling Processing in EA4T Axle Steel

Corrosion fatigue mechanism and life prediction of railway axle EA4T steel exposed to artificial rainwater

An innovative stepwise time-domain fatigue methodology to integrate damage tolerance into system dynamics