A lightweight strain glass alloy showing nearly temperature-independent low modulus and high strength
Chang Liu,Yuanchao Ji,Jingxian Tang,Kazuhiro Otsuka,Yu Wang,Mengrui Hou,Yanshuang Hao,Shuai Ren,Pu Luo,Tianyu Ma,Dong Wang,Xiaobing Ren
DOI: https://doi.org/10.1038/s41563-022-01298-y
IF: 41.2
2022-07-05
Nature Materials
Abstract:Fast development of space technologies poses a strong challenge for elastic materials, which need to be not only lightweight, strong and compliant, but also able to maintain stable elasticity over a wide temperature range 1,2,3,4 . Here we report a lightweight magnesium–scandium strain glass alloy (Mg with 21.3 at.% Sc) that meets this challenge. This alloy is as light (density ~2 g cm –3 ) and compliant as organic-based materials 5,6,7 like bones and glass fibre reinforced plastics, but in contrast with those materials, it possesses a nearly temperature-independent (or Elinvar-type), ultralow Young's modulus (~20–23 GPa) over a wide temperature range from room temperature down to 123 K; a higher yield strength of ~200–270 MPa; and a long fatigue life of over one million cycles. As a result, it exhibits a relatively high, temperature-independent elastic energy density of ~0.5 kJ kg –1 among known materials at a moderate stress level of 200 MPa. We show that its exceptional properties stem from a strain glass transition, and the Elinvar-type elasticity originates from its moderate elastic softening effect cancelling out the ever-present elastic hardening. Our findings provide insight into designing materials that possess unconventional and technologically important elastic properties.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter