Abstract:Activated carbon (AC) fiber is a carbonaceous material with a porous structure that has a tremendous scope of application in different fields. Conventionally, AC is derived from fossil fuel-based raw materials like polyacrylonitrile (PAN) and pitch. In this work, AC was synthesized from eco-friendly, renewable, and ubiquitous jute fiber. Systematically, the jute fiber was washed and pretreated with NaOH. Raw jute and NaOH-treated jute were carbonized/pyrolyzed at 500 °C for 1 h in presence of N2 gas. The carbonized carbon was activated with H3PO4 and KOH and again pyrolyzed at 650 °C for 1.5 h maintaining the inert condition. The different features of activated carbons were characterized with field emission-scanning electron microscope, energy-dispersive X-ray spectroscopy (EDX), transmission electron microscopy (TEM), X-ray diffraction (XRD), and thermogravimetric analysis. The average yield of carbonized and activated carbons was recorded at 19 and 13.8%, respectively. The scanning electron microscopic images confirmed a honeycomb-like porous structure. It was observed that KOH-activated carbon exhibited a more porous structure than the H3PO4-activated carbons. The average pore diameter of activated carbons was noted to be 1.3 μm. The pore density was higher in case of KOH-activated carbons accounting for 2.15 pore/μm. The EDX analysis showed that H3PO4-activated carbons had more than 90% carbon atoms indicating a significant carbon content. The TEM images revealed that AC particles were in the nanoscale range. The average particle sizes of H3PO4-activated carbon and KOH-activated carbon were 36.38 and 32.8 nm, respectively. The XRD study demonstrated the highly disordered and low level of crystallinity of AC. It was detected that the AC showed much higher thermal resistance than the jute fiber. The H3PO4-activated carbon obtained from NaOH-treated jute remained at 84% even after 500 °C. A higher thermal resistance was achieved with H3PO4-activated carbon since it contains 0.56% phosphorus, which was confirmed by EDX investigation. It was found that a higher carbon yield was obtained from NaOH-treated jute. The porous structure of the material showed that it could be used as an adsorbent. Due to its high thermal stability, it is recommended for flame retardants and heat insulation applications as well.

Cotton-Based Activated Carbon Fiber with High Specific Surface Area Prepared by Low-Temperature Hydrothermal Carbonization with Urea Enhancement

Preparation, characterization and adsorption performance of high surface area biomass-based activated carbons

Adsorption of Volatile Organic Compounds on Activated Carbon Fiber Prepared by Carbon Dioxide

Preparation and Characterization of Activated Carbon Fiber (ACF) from Cotton Woven Waste

Synthesis, Activation, and Characterization of Carbon Fiber Precursor Derived from Jute Fiber

Preparation of High Surface Area Activated Carbons from Luffa Cylindrical Sponge by KOH Activation

Cotton-based hollow carbon fibers with high specific surface area prepared by ammonia etching for supercapacitor application

Ultra-large Specific Surface Area Activated Carbon Synthesized from Rice Husk with High Adsorption Capacity for Methylene Blue

The fabrication of porous N-doped carbon from widely available urea formaldehyde resin for carbon dioxide adsorption

Versatile Activated Carbon Fibers Derived from the Cotton Fibers Used as CO2 Solid-State Adsorbents and Electrode Materials

Dye Removal of Activated Carbons Prepared from NaOH-pretreated Rice Husks by Low-Temperature Solution-Processed Carbonization and H3PO4 Activation

Preparation of Nitrogen-containing Activated Carbon from Waste Medium Density Fiberboard for Electric Double Layer Capacitor

Preparation and hydrogen storage of activated rayon-based carbon fibers with high specific surface area

PREPARATION OF ACTIVATED CARBON WITH HIGH SPECIFIC SURFACE AREA FROM CORN COB

Preparation of high specific surface area activated carbon fiber by high-temperature vacuum activation and its superior water vapor adsorption for air humidity control

Optimization of Activated Carbon Fiber Preparation from Hemp Fiber through Dipotassium Hydrogen Phosphate for Application of Thermal Storage System

Ultra-microporous cotton fiber-derived activated carbon by a facile one-step chemical activation strategy for efficient CO 2 adsorption

Preparation of activated carbon fabrics from cotton fabric precursor

Preparation of Biomass Granular Activated Carbon with K2CO3 and Sycamore Tree Sawdust via Dry Mix Process

Tailoring Nitrogen‐Doped Activated Carbons: Central Composite Design for Enhanced CO2 Adsorption

Preparation of High Surface Area Activated Carbon from Spent Phenolic Resin by Microwave Heating and KOH Activation