Sustainable and Facile Route to Nearly Monodisperse Spherical Aggregates of CeO2 Nanocrystals with Ionic Liquids and Their Catalytic Activities for CO Oxidation
Zhen-Xing Li,Le-Le Li,Quan Yuan,Wei Feng,Jun Xu,Ling-Dong Sun,Wei-Guo Song,Chun-Hua Yan
DOI: https://doi.org/10.1021/jp807348n
2008-01-01
The Journal of Physical Chemistry C
Abstract:This article reports a novel preparation of nearly monodisperse spherical aggregates of CeO2 nanocrystals by using ionic liquid (1-hexadecyl-3-methylimidazolium bromide, C(16)MimBr) as both template and solvent. The products were characterized with X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), high-resolution TEM (HRTEM), X-ray photoelectron spectroscopy (XPS), Raman spectroscopy, UV-vis spectroscopy, FT-IR spectroscopy, and N-2 adsorption-desorption methods. The spherical aggregates, with average diameter of 100 - 150 nm, are composed of ca. 3.5 nm CeO2 nanocrystals as building units, giving rise to three-dimensional (313) open porous structures with high Brunauer-Emmett-Teller surface area of 119 m(2).g(-1). Mesoporous CeO2 with surface area up to 227 m(2).g(-1) was prepared by simply tuning the amount of the ionic liquids. Loaded with 5 wt% CuO, both the spherical aggregates and the mesoporous CeO2 exhibit high catalytic activities for CO conversion with 100% conversion rates at low temperature of 150 degrees C, suggesting potential applications in preferential oxidation (PROX) and water-gas shift reaction (WGSR). This sustainable and facile method may be extended to the preparation of other metal oxide nanoarchitectures and provides guidance for structure-controlled synthesis.