Abstract:Red mud, which could cause numerous problems to the environment, is a hazardous waste generated from the alumina smelting industry. In general, the storage and harmless utilization of red mud are hard to implement due to its fine particle size and high alkalinity. This study put forward a novel process to separate iron (MgFe2O4) and alumina (Al2O3) in red mud by a magnetization sintering method. The magnesium oxide was added to transform the nonmagnetic Fe2O3 into magnetic MgFe2O4 to achieve physical separation of iron-bearing minerals, and the alumina-bearing minerals were converted into dissoluble NaAlO2 minerals in a one-step reaction. The atmospheric pressure leaching process was adopted in this study for alumina resource recovery. To achieve clean alumina production, the silicate in the leaching solution was removed by adding the slightly soluble CaSO4, and the entire process becomes clean and harmless. The feasibility of the process was verified by thermodynamic analysis, and a series of experiments were performed to detect the optimum MgO/(Fe2O3 + MgO) ratio and the calcining and leaching conditions. The morphological and mineralogical characteristics of modified red mud, leaching red mud, and magnetic separation product were studied by X-ray diffraction analysis (XRD) and scanning electron microscopy (SEM) energy dispersive spectroscopy (EDS). It was observed that under the optimal conditions with MgO/(Fe2O3 + MgO) of 14.89% to recover iron and aluminum, the corresponding recovery rates were 67.54% and 73.01% respectively, and the iron grade was 30.46%. The EDS results showed that the obtained Mg/Fe ratio of the magnetic separation product was 0.4677–0.528, which is slightly different from that of the standard MgFe2O4 at 0.5. This new method can promote the development of comprehensive utilization of red mud and iron production.

Increasing Iron Recovery from High-Iron Red Mud by Surface Magnetization

Recovery of iron from high-iron red mud using suspension magnetization roasting and magnetic separation

Clean utilization of high-iron red mud by suspension magnetization roasting

Extraction of Iron and Alumina from Red Mud with a Non-Harmful Magnetization Sintering Process

Iron Extraction from Red Mud using Roasting with Sodium Salt

Study on Magnetization Roasting Kinetics of High-Iron and Low-Silicon Red Mud

High‐efficiency Preparation of Fe–Al Based Flocculants from Red Mud by Microwave Selective Carbothermic Reduction and Magnetic Separation

Stepwise extraction of valuable components from red mud based on reductive roasting with sodium salts

Iron Recovery from Red Mud Using Carbothermic Roasting with Addition of Alkaline Salts

An Novel Method for Iron Recovery from Iron Ore Tailings with Pre-Concentration Followed by Magnetization Roasting and Magnetic Separation

Improved iron recovery from low-grade iron ore by efficient suspension magnetization roasting and magnetic separation

Modeling Assessment of Recovering Iron from Red Mud by Direct Reduction: Magnetic Separation Based on Response Surface Methodology

Efficient enrichment of iron concentrate from iron tailings via suspension magnetization roasting and magnetic separation

Investigation of the smelting reduction mechanism and of iron extraction from high-iron red mud

Optimizing iron separation and recycling from iron tailings: A synergistic approach combining reduction roasting and alkaline leaching

Cleaning Disposal of High-Iron Bauxite Residue Using Hydrothermal Hydrogen Reduction

Extraction of Scandium and Iron from Red Mud

Enhanced iron extraction from high-phosphorus waste limonite ore via suspension magnetization roasting: A pilot-scale study

Producing magnetite concentrate from iron tailings via suspension magnetization roasting: A pilot-scale study

An efficient and green method to separate iron and manganese from ferromanganese ore by suspension magnetization roasting and magnetic separation

Experimental Research on Vortex Melting Reduction of High-Iron Red Mud (Bauxite Residue)