Seed-assisted synthesis of Ga-MFI slabs and nanocrystal agglomerates and comparative study of acidic properties
Sen Lin,Fanyong Meng,Lin Sun,Runwei Wang
DOI: https://doi.org/10.2139/ssrn.4307879
IF: 5.876
2023-03-05
Microporous and Mesoporous Materials
Abstract:A series of Ga-MFI zeolites were one-step synthesized following the seed-assisted strategy without using additional organic template. The effects of synthesis parameters on the framework fabrication, morphology evolution, and gallium incorporation were systematically investigated by XRD, N 2 -adsorption, UV-Raman, STEM, TEM, solid state NMR, NH 3 -TPD, and Py-IR analyses. The Si/Ga seed exhibited a highly efficient structure-directing capability in the assembly of MFI framework and the amount of the costly tetrapropylammonium hydroxide (TPA + ) was thus decreased to less than one-tenth in comparison with the traditional synthesis. Crystallization temperature and pre-aging conditions played the key roles in the Ga-MFI zeolite synthesis. Both of the morphology and the intraframework gallium concentration can be facilely controlled by adding the mineralizer and surfactant. The addition of NH 4 F and CTAB was favorable for the formation of the slabs-form product but against to the gallium substitution. Only with the help of Si/Ga seed, the synthesized Ga-MFI nanocrystal agglomerates possess a highly accessible hierarchical mesopore structure that consisted solely of interparticle-type mesopores. Simultaneously, it also exhibited a remarkable gallium incorporation, which ensured the great acidic properties, including strong acidic strength and high acid amount. As a consequence, the Ga-MFI nanocrystal agglomerates performed the excellent catalytic activity in the LDPE degradation.
materials science, multidisciplinary,chemistry, physical,nanoscience & nanotechnology, applied