One-step synthesis of magnetic asphalt-based activated carbon with high specific surface area and adsorption performance for methylene blue

Qianyu Wang,Emmanuel Oluwaseyi Fagbohun,Houkun Zhu,Abid Hussain,Fang Wang,Yanbin Cui

DOI: https://doi.org/10.1016/j.seppur.2023.124205

IF: 8.6

2023-06-08

Separation and Purification Technology

Abstract:A novel magnetic asphalt-based activated carbon (MAAC) had been prepared by a facile one-step method and the adsorption to methylene blue (MB) was also investigated. Textural characteristics of the prepared MAAC were evaluated by various analytical techniques such as BET, VSM, FT-IR, XRD, and SEM/EDS. The results show that MAAC were endowed with a micro/mesoporous structure. The MAAC-800–4 (4:1 of KOH/asphalt and calcination at 800 °C) had a maximum BET surface area of 2880 m 2 ·g −1 and a maximum total pore volume of 1.809 cm 3 ·g −1 , and the saturation magnetization (Ms) was measured to be 15.81 emu·g −1 . There was an abundant oxygen functional group (–OH, C–O, –COO–) on the MAAC-800–4 surface, and zero-valent iron was uniformly dispersed and embedded in the carbon matrix. Batch adsorption tests showed that the maximal adsorption capacity (q m ) of MAAC-800–4 for MB is 710 mg·g −1 at 25 °C. Langmuir isotherm and pseudo-second-order kinetic model best fit the experimental data. Thermodynamic parameters indicated that the adsorption process was spontaneous and endothermic. The adsorption capacity of MAAC-800–4 for MB retained over 66% of its initial adsorption capacity after five regeneration cycles. These findings suggest that the MAAC would be a promising efficient adsorbent for treating organic wastewater.

engineering, chemical