Sintering parameter optimization of Tb 3 Al 5 O 12 magneto‐optical ceramics by vacuum sintering and HIP post‐treatment

Xiaoying Li,Qiang Liu,Xin Liu,Danyang Zhu,Dianjun Hu,Feng Tian,Lexiang Wu,Zhaoxiang Yang,Tengfei Xie,Haohong Chen,Jiang Li

DOI: https://doi.org/10.1111/jace.17628

IF: 4.186

2021-01-25

Journal of the American Ceramic Society

Abstract:<p>Transparent terbium aluminum garnet (TAG) ceramics were achieved by the vacuum sintering plus HIP post‐treating from the co‐precipitated TAG nanoparticles. The influences of vacuum sintering temperature and sintering aid TEOS on the optical quality of the TAG ceramics were studied. The results show that with the increase of sintering temperature, the optical quality of TAG ceramics is improved gradually, and the in‐line transmittance of the TAG ceramics treated at 1720°C for 20 h under vacuum and then HIP post‐treated at 1700°C for 3 h under 200 MPa argon gas is 81.6% at 1064 nm. The sintering additive TEOS can improve the optical quality of TAG ceramics and inhibit the valence state change of Tb³⁺ ions to Tb⁴⁺ during the annealing process. The Verdet constant of the TAG ceramics at 632.8 nm is about ‐178 rad·T^‐1·m^‐1 at room temperature, which is 1.3 times that of the commercial TGG crystals (‐134 rad·T^‐1·m^‐1).</p>

materials science, ceramics

What problem does this paper attempt to address?

The problem that this paper attempts to solve is how to prepare high - quality Tb₃Al₅O₁₂ (TAG) magneto - optical ceramics by optimizing sintering parameters. Specifically, the paper studies the influence of vacuum sintering temperature and sintering aid TEOS on the optical properties of TAG ceramics. The main objective is to improve the optical transparency and Verdet constant of TAG ceramics to meet the requirements for miniaturization and high - performance magneto - optical isolators in high - power laser systems.

The key points mentioned in the paper include:
1. **Influence of Sintering Temperature**: The optical quality and microstructure changes of TAG ceramics at different vacuum sintering temperatures were studied. It was found that as the sintering temperature increases, the optical quality of TAG ceramics gradually improves, but it will decrease after exceeding a certain temperature.
2. **Role of Sintering Aid TEOS**: TEOS, as a sintering aid, can significantly improve the optical quality of TAG ceramics and inhibit the valence change of Tb³⁺ ions during the annealing process, thus avoiding ceramic discoloration.
3. **Microstructure Analysis**: The microstructures of TAG ceramics under different sintering conditions were observed by FESEM. It was found that as the sintering temperature increases, the grain size increases, but when the temperature exceeds 1600 °C, the change in grain size tends to be flat.
4. **Optical Performance Testing**: The transmittance and Verdet constant of TAG ceramics under different conditions were measured. The results show that the TAG ceramics prepared under the best conditions have a transmittance of 81.6% at 1064 nm and a Verdet constant of - 178 rad·T⁻¹·m⁻¹, which is approximately 33% higher than that of commercial TGG single crystals.

Overall, this paper aims to prepare TAG magneto - optical ceramics with high optical quality and high Verdet constant by optimizing sintering parameters, especially the use of sintering temperature and sintering aids, to meet the requirements for high - performance magneto - optical materials in high - power laser systems.