Comparative Analyses of the Influence of TEOS Additives on the Sintering Kinetics of Nd: YAG Transparent Ceramics

Wentao Jia,Qinlei Wei,Hongbo Zhang,Chunhui Su,Guozhong Ren,Mengjie Zhao,Chaoyu Ma
DOI: https://doi.org/10.21203/rs.3.rs-303180/v1
2021-03-17
Abstract:Abstract In this work, the sintering kinetics of Nd: YAG transparent ceramics under the vacuum environment was studied by the high-temperature solid phase method. The effects of different sintering temperatures and TEOS content on the densification process of Nd: YAG ceramics were studied. Meanwhile, the crystal structure of Nd: YAG transparent ceramics doped with different contents of TEOS was studied by X-ray diffractometer (XRD) and differential thermal analysis (DTA). The micrographs of ceramics samples were analyzed by scanning electron microscope (SEM). The green sample is heated to 1450~1650°C for 0~2 h at a heating rate of 20°C/min in a vacuum environment (P T ≤ 10 -6 Pa), and the shrinkage of ceramic samples was analyzed in the vacuum atmosphere by the Johnson sintering model. The sintering activation energy of Nd: YAG transparent ceramics doped with different contents of TEOS was obtained. The results indicated that the addition of TEOS promoted the densification of ceramic samples. The grain size and relative density of ceramic samples increased, and the sintering activation energy decreased with the increase of TEOS content.
What problem does this paper attempt to address?