Abstract:To address the issue of inadequate strength and plasticity in magnesium matrix composites, SiC preforms were prepared using the freeze-casting process. The effects of sintering temperature on the microstructure, mechanical properties, and fracture behavior of SiCp/AZ91 magnesium matrix composites were studied by controlling the density of SiC preforms through low-temperature sintering. The results indicate that as the sintering temperature decreases, the reaction products in the SiC layer decrease, resulting in lower SiC preform density and increased content of AZ91 alloy filling in the layer. The increased alloy content in the ceramic layer not only inhibits crack initiation but also hinders crack propagation, thereby endowing the SiCp/AZ91 laminated material with excellent compressive strength and compressive strain. At the sintering temperature of 900 °C, the SiCp/AZ91 laminated material exhibits impressive compressive strength and strain values of 623 MPa and 8.77%, respectively, which demonstrates an excellent combination of strength and toughness.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,metallurgy & metallurgical engineering
What problem does this paper attempt to address?
The problem this paper attempts to address is the deficiency in strength and plasticity of magnesium-based composites. Specifically, the researchers studied the effects of different sintering temperatures on the microstructure, mechanical properties, and fracture behavior of SiCp/AZ91 magnesium-based composites by adjusting the density of the ceramic layer. The aim is to optimize the compressive strength and compressive strain of the composite material by controlling the density of the SiC preform, thereby achieving a balance between high strength and high toughness.
The research background points out that although magnesium and its alloys have great application potential in aerospace, automotive, electronics, and other fields due to their low density and high specific strength and stiffness, their absolute strength and elastic modulus are relatively low, limiting their practical applications. To overcome this issue, researchers typically add reinforcing particles (such as TiC, SiCp, etc.) to prepare particle-reinforced magnesium-based composites (PMMCs). These composites exhibit high modulus, high strength, and excellent wear resistance. However, as the content of reinforcing particles increases, although the modulus of the composite material significantly improves, its plasticity decreases, which becomes one of the key issues that need to be addressed in the development of magnesium-based composites.
Therefore, the focus of this study is to optimize the mechanical properties of the composite material, particularly improving its strength and toughness, by controlling the sintering temperature to adjust the looseness of the ceramic layer. The research results show that at a sintering temperature of 900°C, the SiCp/AZ91 layered material exhibits a compressive strength of 623 MPa and a compressive strain of 8.77%, demonstrating an excellent combination of strength and toughness.