Abstract:A combined steady-state and transient approach is employed to investigate the corrosion behavior of X80 pipeline steel in carbon dioxide-saturated brines. Continuous bubbling of carbon dioxide into a test vessel with 1 liter capacity is performed to simulate the flowing condition. The measurement of time-dependent open-circuit potential, polarization resistance, and electrochemical impedance spectroscopy (EIS) is conducted to interpret the evolution of dissolution processes at the corroding interface. Three distinguishing stages are observed at a temperature of 60 °C during a whole exposure of 144 h. Analyses mainly based on the consecutive mechanism show that after the first stage of the active-adsorption state, the anodic reaction is significantly retarded by the accumulation of (FeOH)ads on the iron surface, causing a sharp increase in the polarization resistance and the open-circuit potential, as well as the disappearance of the inductive loop in EIS. At the third stage, the formation of the corrosion product layer similarly reduces both the anodic and cathodic reactions, which arouses a linear increase in the polarization resistance with time and a capacitive loop in EIS but changes the open-circuit potential slightly. An increase in salinity in this study reduces the polarization resistance and enhances iron dissolution by promoting the formation and relaxation of (FeOH)ads; however, it brings little change to the developing time of the three stages obviously. At a low temperature of 20 °C, a protective product layer is not observed in carbon dioxide-saturated brine, and the dissolution of iron is mainly under activation control during the whole exposure. A notable enlarged polarization resistance and different interfacial processes are observed in an alkaline solution compared with those in acidic environments, which is deduced to be resulted from an impedance in the relaxation of (FeOH)ads by increasing pH. The observations in this study support well that the iron dissolution reaction at the initial stage exposed in carbon dioxide aqueous environments is dominant by water adsorption on the iron surface, and further investigation should be performed on the role that carbon dioxide plays in the evolution of corrosion products and the formation of a protective film on the steel surface by taking into account local water chemistry.

Research on dynamic AC corrosion behavior of X65 Pipeline Steel under cathodic protection

Research on AC corrosion behavior and corrosion product film evolution of X70 steel under the combined action of AC interference and CP

Effects of Alternating Current Interference on the Cathodic Protection for API 5L X60 Pipeline Steel

Combined Effect of Alternating Current Interference and Cathodic Protection on Pitting Corrosion and Stress Corrosion Cracking Behavior of X70 Pipeline Steel in Near-Neutral pH Environment

Experimental research on the corrosion of X series pipeline steels under alternating current interference

AC corrosion of steel pipeline under cathodic protection: A state‐of‐the‐art review

Effect of Alternating Current on Passive Film and Corrosion Behavior of Pipeline Steel with Different Microstructures in Carbonate/Bicarbonate Solution

AC corrosion behavior and the effect of stone-hard-soil on corrosion process in the earth alkaline rich environment

Corrosion Behavior of X80 Steel in a Simulated Soil Solution Under Square-Wave Current Interference

AC Corrosion of Carbon Steel under Cathodic Protection Condition: Assessment, Criteria and Mechanism. A Review

The influence of half-cycle rectified sinusoidal alternating current (AC) on corrosion of X80 pipeline steel in an acid bicarbonate solution

<i>Technical</i><i> Note:</i> Study on Accelerated Corrosion Behavior and Mechanism of X80 Pipeline Steel Welded Joint Under Cyclic Salt Spray Test

Electrochemical and Stress Corrosion Mechanism of Submarine Pipeline in Simulated Seawater in Presence of Different Alternating Current Densities

Stress corrosion cracking behavior of X80 pipeline steel under alternating current, Desulfovibrio desulfurican and cathodic protection potential

Research on corrosion rate assessment of buried pipelines under dynamic metro stray current

Cathodic Protection of X100 Pipeline Steel in Simulated Soil Solution

Study on accelerated corrosion behavior and mechanism of X80 pipeline steel welded joint under cyclic salt spray test

Experimental Investigation on Corrosion Behavior of X80 Pipeline Steel under Carbon Dioxide Aqueous Conditions

Effects of Alternating Stray Current on the Corrosion Behaviours of Buried Q235 Steel Pipelines

STUDY ON THE ACCELERATED CORROSION BEHAVIOR OF A GALVANIZED X80 PIPELINE STEEL WELDED JOINT DURING A CYCLIC SALT SPRAY TEST

Corrosion of Steel Embedded in Mortar and Concrete under Different Electrolytic Accelerated Corrosion Methods