Abstract:Corrosion of steel reinforcements degrades the structural performance of reinforced concrete (RC) columns under static and seismic loads. Such corroded RC columns are usually retrofitted with fiber-reinforced polymer (FRP). However, existing studies on the retrofitting of RC columns with corrosion and load-induced damage are limited. To confirm the effectiveness of basalt FRP (BFRP) jacketing on the compressive behavior of corroded and pre-damaged RC columns, this study performed axial compression tests on eleven circular RC columns. The columns were fabricated, corroded, pre-damaged, and then jacketed with BFRP composites and reloaded to investigate the effects of BFRP layer number, corrosion ratio, and pre-damage degree. When jacketed by BFRP, the ultimate strength and ultimate strain of RC columns increased with BFRP layer numbers, ranging from 5% to 98% and 448% to 926%, respectively. Further, the ultimate strength and elastic modulus of the jacketed RC columns decreased with the increase in pre-damage degrees and corrosion ratios, while the ultimate strain was little affected. Buckling and corrosion of longitudinal bars significantly reduced the bar stresses at the ultimate state of BFRP-jacketed RC columns and resulted in local rupture of BFRP. This adverse effect became more pronounced as the corrosion ratio increased, but was alleviated by BFRP jacketing. On the other hand, a refined rebar stress-strain model was developed by addressing the effects of buckling, corrosion, and lateral confinement. Further, a feasible constitutive model for corroded hoop-confined columns was determined by validating the existing test results. Finally, models for the ultimate strength, ultimate strain, and stress-strain response of BFRP-jacketed corroded and pre-damaged RC columns were developed.

Compressive behavior of corroded reinforced concrete columns strengthened with BFRP reinforced ECC in marine environment

A critical assessment of the compressive behavior of reinforced recycled aggregate concrete columns

Effectiveness of CFRP Confinement and Compressive Strength of Square Concrete Columns

Axial compressive behavior and model analysis of BFRP-jacketed corroded and pre-damaged circular reinforced concrete columns

Axial Compressive Behavior of FRP-confined Square CFST Columns Reinforced with Internal Latticed Steel Angles for Marine Structures

Corroded reinforced concrete columns strengthened with basalt fibre reinforced ECC under axial compression

Compressive behavior degradation of FRP-confined RC columns exposed to a chlorine environment

Study on the Corroded Hollow Section RC Columns Strengthened by ICCP-SS System

Experimental-numerical study on axial compression performance of square concrete columns confined by new-type BFRP

Effects of Reinforcement Corrosion and Sustained Load on Mechanical Behavior of Reinforced Concrete Columns.

CFRP Strengthened RC Beams with Pre-Strengthening Non-Uniform Reinforcement Corrosion Subjected to Post-Strengthening Wetting/drying Cycles

Shear strengthening of corroded reinforced concrete columns using pet fiber based composties

Mechanical Degradation of Reinforced Concrete Columns Corroded Under Sustained Loads

FRP-confined Concrete Core-Encased Rebar for RC Columns: Concept and Axial Compressive Behavior

Compressive Behavior of Composite Concrete Columns with Encased FRP Confined Concrete Cores.

Compressive behavior of RC columns strengthened with FRP and prefabricated UHPC blocks

Experimental Study on Eccentric Compressive Performance of Concrete Column Strengthened with CFRP Grid Reinforced ECC Matrix

Anti-corrosion performance of a novel ECC-GFRP spiral-confined RC column

Seismic Performance of Corroded ECC-GFRP Spiral-Confined Reinforced-Concrete Column

Axial compression behaviour of seawater sea sand concrete columns reinforced with hybrid FRP-stainless steel bars

Experimental investigation of corrosion-damaged RC beams strengthened in flexure with FRP grid-reinforced ECC matrix composites