Desorption behavior and mechanism of yttrium ions from ion-adsorption type rare earths ore
Xindi Guan,Ping Li,Jikai Zhang,Qingqing Chang,Yunwu Han,Hailin Zhang,Qian Li,Jiachun Xiong,Wei Zhao,Shili Zheng
DOI: https://doi.org/10.1016/j.seppur.2024.126283
IF: 8.6
2024-01-05
Separation and Purification Technology
Abstract:Ion-adsorption type rare earths ore (IREO) is an important strategic resource that can be leached in-situ using electrolytes such as NH 4 + , Mg 2+ , and Al 3+ . However, the use of NH 4 + was restricted due to ammonia-nitrogen pollution, regarding in-situ leaching agents still remain controversial. It is imperative to comprehensively and systematically investigate the desorption mechanism of rare earth elements (REEs) from a microscopic perspective, especially when using Mg 2+ and Al 3+ as leaching agents. In this manuscript, the desorption behavior and mechanism of Y 3+ from ADY (IREO as adsorbents loaded with Y 3+ ) were studied, along with a comparison of the Y 3+ desorption capabilities of Mg 2+ and Al 3+ as leaching agents. The results showed that Y 3+ could be effectively desorbed from IREO by both Mg 2+ and Al 3+ , with Y 3+ desorption yields of 93.1 % (pH 3.2, 0.06 mol/L) for Al 3+ and 88.6 % (pH 6.0, 0.3 mol/L) for Mg 2+ , respectively. The superior Y 3+ desorption capability of Al 3+ arises from its higher valence, greater electronegativity, and smaller ionic radius compared to Mg 2+ . The higher valence imparts Al 3+ greater charge density, while the greater electronegativity enables Al 3+ to more readily substitute for Y 3+ . Additionally, the smaller ionic radius facilitates the entry of Al 3+ into clay minerals interlayers. At high H + concentrations, the Y 3+ desorption capabilities of Mg 2+ and Al 3+ were both higher than at the original pH without acid addition, primarily due to the influence of H + , which could leach Y 3+ from the un-exchangeable phase, but also significantly increased the leaching of impurities. The isotherms and kinetics demonstrated the desorption of Y 3+ in the case of Mg 2+ and Al 3+ existing followed the Langmuir and pseudo-second-order models, indicating homogeneous, chemisorption-governed processes. Furthermore, ATR-FTIR, XPS, and DFT results revealed Y 3+ desorption occurred by breaking SiOY bonds and ion exchange with Mg 2+ /Al 3+ to form SiOMg/Al bonds.
engineering, chemical