Abstract:The paper substantiates the composition and prospects of using high strength Al–Zn–Mg–Ca–Fe casting aluminum alloy without heat treatment based on the study on the structure, technological and mechanical properties. Alloys of the base composition Al–5.5%Zn–1.5%Mg (wt.%) jointly and separately doped with 0.5–1.0 % Ca and 0.5 % Fe were obtained as the objects of research. Standard casting alloys according to GOST 1583-93: AK12M2, AMg6lch, AM4,5Kd were the objects of comparison. A hot tensile test using a cast test bar was conducted to check the tendency to form hot cracks due to hindered contraction. It was shown that separate alloying with calcium and iron does not contribute to the improvement of crack resistance and adversely affects mechanical properties. Combined alloying with 1 % Ca and 0.5 % Fe improves the hot tearing resistance to the level of the AMg6lch alloy properties. This effect is due to calcium-containing phases of eutectic origin formed and a favorable grain structure created that is free from columnar grains. Iron in the alloy structure is bound in compact Al 10 CaFe 2 phase particles as a result of the non-equilibrium crystallization during permanent mold casting. The formation of this phase allowed to reduce the amount of zinc in the (Al, Zn) 4 Ca phase and mostly retain the (Al) solid solution composition as evidenced by similar hardness values of the Al–5.5%Zn–1.5%Mg base alloy and Al–5.5%Zn–1.5%Mg–1%Ca–0.5%Fe alloy, and the superiority of the values over the hardness of alloys separately alloyed with calcium and iron. Also the cast hardness of the promising alloy more than 20 HV higher than the cast hardness of commercial cast alloys. The new alloy in the as-cast condition exhibited competitive mechanical tensile properties: UTS ~ 310 MPa, YS ~ 210 MPa, El ~ 4 %.

Aluminum-lithium alloys: types, properties, application, and production technologies. Overview

Trends in the development of aluminum alloys for power elements of aviation egineering components within Russia and abroad. Review

Advanced aluminium alloys for aircraft and aerospace applications

Research Progress of New Generation of Aluminum‐Lithium Alloys Alloying

Development and Application Prospects of Aluminum–Lithium Alloys in Aircraft and Space Technology

Physical metallurgy of aluminum-lithium alloys

Arc-Welding: Lithium-Containing Aluminum Alloys

A review of manufacturing processes, mechanical properties and precipitations for aluminum lithium alloys used in aeronautic applications

Mechanical Properties of a Novel High-Strength Aluminum-Lithium Alloy

Multicomponent Aging Al-Li-Based Alloys of the Latest Generation: Structural and Phase Transformations, Treatments, Properties, and Future Prospects

Mechanical behaviour of aluminium-lithium alloys

Developing a novel lightweight Al–Mg–Li alloy for laser powder bed fusion additive manufacturing: Parameter optimization, microstructure evolution, and mechanical performance

Aircraft Aluminum Alloys: Applications and Future Trends

Aluminum-Copper-Lithium Alloy 2050 Developed for Medium to Thick Plate

Microstructure and Mechanical Properties of Al-Li Alloys with Different Li Contents Prepared by Selective Laser Melting

New high-strength casting aluminum alloy based on the Al–Zn–Mg–Ca–Fe system without requirement for heat treatment

Recently-Developed Aluminium Solutions for Aerospace Applications

Structure and properties of industrial semi-products of weldable corrosion-resistant Al – Mg – Si – Cu system aluminum alloy

Investigation of the Effect of Modifying the AlSi7Mg0.3 Alloy with a Fast-Cooled Master Alloy Using Heat Treatment

New high-strength aluminum alloy on the basis of secondary materials

Thermodynamic and Kinetic Calculation of High Strength Aluminum-Lithium Alloy