Abstract:In order to improve the overall performance of edge plates such as bulldozer blades, composition and heat treatment processes were optimized on the martensitic wear-resistant steel grade 400 HB. Steel billets were first obtained through smelting in a state of hot rolling, followed by quenching and tempering to obtained wear-resistant steel (HB400). Then, HB400 was subjected to metallographic observation, electron backscatter diffraction (EBSD) testing, and transmission electron microscope (TEM) characterization and property testing. The results showed that HB400 exhibited microstructural refinement, characterized by narrower martensite laths and finer grains. The EBSD results indicated a uniform microstructure with a low content of the residual austenite (0.5%), indicating good hardenability. TEM observation of the martensite matrix revealed the presence of substructures, i.e., numerous dislocations in martensite laths. The average Rockwell hardness (HRC) of HB400 was 46.3, and the average Brinell hardness (HB) was 402. A mechanical properties test demonstrated comprehensive properties, which showed that the ultimate tensile strength and yield strength of HB400 were 1495 MPa and 1345 MPa, respectively, with a relative elongation of 12%. Friction and wear experiments showed that the friction coefficient and wear rate in reciprocating mode decreased by 16.1% and 45.4%, respectively, while in rotating mode, they decreased by 27.6% and 2.1%, respectively, as the load increased from 100N to 300N. According to the wear morphology, the main wear mechanisms were identified as adhesive wear, abrasive wear, and oxidative wear. The lubricating effect of the oxide layer generated by wear was identified as the primary reason for the reduction in the friction coefficient. The relationship between microstructures and properties was discussed based on grain refinement strengthening and dislocation strengthening.

INFLUENCE OF TEMPERING TEMPERATURE ON THE ABRASIVEWEAR OF HIGH-STRENGTH, MARTENSITIC BORON STEELHARDOX EXTREME

Analysis of the possibilities to increase abrasion resistance of welded joints of Hardox Extreme steel

Effect of tempering on the impact-abrasive and abrasive wear resistance of ultra-high strength steels

Comparative Analysis of the Influence of Chemical Composition and Microstructure on the Abrasive Wear of High-Strength Steels

High-stress abrasive wear characteristics of ultra-high strength press-hardening steel

Resistance to Abrasive Wear with Regards to Mechanical Properties Using Low-Alloy Cast Steels Examined with the Use of a Dry Sand/Rubber Wheel Tester

The influence of austenitizing temperature on prior austenite grain size and resistance to abrasion wear of selected low-alloy boron steel

On Microstructure and Performance of Tempered High-Boron High-Speed Steel Roll

Study on the Microstructure and Mechanical Properties of Martensitic Wear-Resistant Steel

Study of the Effects on the Strengthening Mechanism and Wear Behavior of Wear-Resistant Steel of Temperature Controlling in Heat Treatment

Analysis of Tribological Properties of Hardfaced High-Chromium Layers Subjected to Wear in Abrasive Soil Mass

Effect of hardenability on microstructure and property of low alloy abrasion-resistant steel

Influence of Heat Treatment on Wear Resistant of High Boron Casting Steel

Austenite Grain Growth Analysis in a Welded Joint of High-Strength Martensitic Abrasion-Resistant Steel Hardox 450

Study on the effect of tempering on the impact abrasive wear performance of 45Si2MnCr2Mo ultra-high strength steel

Investigation of the Effect of Tempering and Cryogenic Treatment on Mechanical Properties of Boron Steels

Abrasive Wear Mechanisms of S235JR, S355J2, C45, AISI 304, and Hardox 500 Steels Tested Using Garnet, Corundum and Carborundum Abrasives

Effect of Heat Treatment on Structure and Wear Resistance of High Chromium Cast Steel Containing Boron

Effect of Chromium on Microstructure and Oxidation Wear Behavior of High-Boron High-Speed Steel at Elevated Temperatures

Effect of Short-Term Low-Temperature Austempering on the Microstructure and Abrasive Wear of Medium-Carbon Low-Alloy Steel

Effect of heat treatment on mechanical properties of 1500MPa high strength wear-resistant steel