COMPARISON OF THE MECHANICAL PROPERTIES, HEAT PERMEABİLİTY CHARACTERISTICS AND RESISTANCE AGAINST HIGH TEMPERATURE OF LIGHT MORTARS MADE WITH EPS AND WASTE POLYURETHANE

Halil EREN,Serhan İLKENTAPAR,Uğur DURAK
DOI: https://doi.org/10.21923/jesd.935865
2022-06-30
Mühendislik Bilimleri ve Tasarım Dergisi
Abstract:In this study, the use of waste polyurethane released after industrial processing in light mortar production has been investigated. Lightweight mortar samples were produced using EPS (Expanded polystyren foam) and waste polyurethane, which are currently used in lightweight mortar production. The produced samples were compared according to their equivalent unit weights and the use of waste and polyurethane in light mortar production was examined. Within the scope of the study, 40x40x160 mm prismatic mortar samples were produced by replacing 20%, 40%, 60%, 80%, 100% by volume with EPS and waste polyurethane aggregate.The unit weight values, ultrasonic pulsed wave velocities, thermal conductivity coefficients and flexural and compressive strengths of the produced mortar samples were measured. In addition, mortar samples produced with both EPS and waste polyurethane were subjected to high temperatures at 3000C, 6000C, 9000C, and then the mechanical strength and microstructures of the samples were examined. Microstructure studies were performed on dough samples with FESEM images. According to the data obtained, it has been concluded that mortars produced with waste polyurethane perform better than mortars with EPS in both medium strength lightweight concrete mortars and mortars in the carrier light concrete class. Especially when the mechanical strengths after high temperature are examined, it has been determined that waste polyurethane mortar samples give higher flexural and compressive strengths compared to EPS samples.
What problem does this paper attempt to address?