Bulk doping nickel–cobalt metal organic framework nanosheet arrays for performance-boosted hybrid supercapacitors

Guosheng Wang,Zhaoxiong Yan,Nenghuan Wang,Ming Xiang,Zhihua Xu,Huilin Zhu

DOI: https://doi.org/10.1557/s43578-022-00567-5

IF: 2.7

2022-05-03

Journal of Materials Research

Abstract:Bulk doping nickel–cobalt metal–organic framework (NiCo-MOF) nanosheet arrays were prepared by a one-pot hydrothermal method. The NiCo-MOF with Ni/Co molar ratio of 1:1 (NiCo-MOF-1:1) possessed a superior capacity of 151.9 mA h g–1 at 0.5 A g–1, and excellent high-rate property with only reduced 10.8% of the capacity as increasing the current density from 0.5 to 8 A g–1. The assembled hybrid supercapacitor with NiCo-MOF-1:1 as a positive material and activated carbon (AC) as a negative material, exhibited an optimal energy density of 28.6 W h kg–1 at a power density of 433.2 W kg–1, and relatively stable cycling capability after 5000 cycles. A larger exposed active area, lower transfer resistance and rapider ion diffusion induced by the crystal distortion and alteration of morphology and textural structure were primarily responsible for the enhanced electrochemical performance of NiCo-MOF-1:1 in contrast to the monometallic (Ni or Co) MOF.Graphical abstractBulk doping nickel–cobalt metal organic framework (NiCo-MOF-1:1) nanosheet arrays prepared via an one-pot hydrothermal method showed enhanced capacitive performance compared with Ni-MOF and Co-MOF alone

materials science, multidisciplinary