One-pot fabrication of Ni/Co-MOFs/GNS nanohybrid as electrode material with high performance
Tian-Li Meng,Ying-Xia Ma,Jia-Wei Wang,Xiao-Dan Zhang,Lei Lei,Jing Li,Fen Ran
DOI: https://doi.org/10.1007/s10854-024-13352-3
2024-08-19
Journal of Materials Science Materials in Electronics
Abstract:Metal–organic frameworks (MOFs) are supposed to be promising electrode materials for supercapacitors for the excellent porosity, variable pore size, and structural variety. Bi-metal MOFs have higher electrochemical performances compared to the corresponding single-metal MOFs as various metal ions could provide an increased number of electron transfer paths and active sites. Nevertheless, inferior stability and unsatisfactory electroconductivity of bi-metal MOFs greatly restrict further applications. In this work, using graphite nanosheets (GNS) as supports, Ni/Co-MOFs were loaded on the GNS by in situ growth to fabricate Ni/Co-MOFs/GNS nanohybrids via a one-pot solvothermal method. GNS as carbon materials have good electroconductivity and stability. Ni/Co-MOFs loaded on the GNS by in situ growth could avoid Ni/Co-MOFs aggregation and improve the dispersity, increasing the specific surface area and exposing more redox active sites, resulting in improvement of the electrochemical performances. The electrochemical performances of Ni/Co-MOFs/GNS were optimized by altering the molar ratio of Co(NO 3 ) 2 ·6H 2 O to Ni(NO 3 ) 2 ·6H 2 O and the condition of the reaction. According to the research findings, the Ni/Co-MOFs/GNS nanohybrid had a higher specific capacity which was 1080.0 C g −1 at 1 A g −1 . Active carbon (AC) serving as the negative electrode and Ni/Co-MOFs/GNS as the positive electrode, Ni/Co-MOFs/GNS//AC asymmetric supercapacitor (ASC) was assembled. The energy density of Ni/Co-MOFs/GNS//AC ASC was 28.7 Wh kg −1 and the power density was 849.9 W kg −1 .
engineering, electrical & electronic,materials science, multidisciplinary,physics, condensed matter, applied