Abstract:AZ31B magnesium alloy and 6061 aluminum alloy of 0.2 mm thickness were joined by nanosecond pulsed laser welding technology, and the effects of nanosecond pulsed laser power on the formation of weld seam, interface microstructure and mechanical properties were investigated, and numerical simulation of the temperature field during the welding process was carried out. The results show that when the laser power is 50 W, more defects such as cracks, pores and sags appeared in the joints due to the high heat input, and these defects resulted in a smaller effective joint area between the metals, which is very unfavorable to the strength of the joints. As the laser power decreases, at a laser power of 25 W, fewer defects are exhibited and the effective joint area becomes larger. As the laser power continues to decrease, the low heat input makes metal melting and joining very difficult. At low laser power, the Mg element intrudes backwards into the aluminum, causing the joint boundary interface to take on a reverse "V" shape. According to the results of the tensile shear experiments, the maximum tensile force of the joint was the highest at a laser power of 25 W, which reached 76.5 N. In addition, it was observed that the effective joint area, the number of oxides and their inclusions, and the degree of angular deformation had a very important effect on the mechanical properties of the joints. The results of temperature field numerical simulation experiments show that the heat is accumulated from outside to inside during the laser scanning process, and whether the temperature in the center of the molten pool reaches the melting point of the alloy can be used as an important basis for analyzing the degree of welding.

Effect of laser power on microstructure and mechanical properties of laser heat conduction lap welded joint between AZ31B magnesium alloy and DP780 galvanized steel

Effect of nanosecond pulse laser power on welding interface and mechanical properties of AZ31B Mg/6061 Al

Microstructure and Mechanical Properties of Laser Welded Magnesium Alloy/Steel Joint Using Cu-Si Composite Interlayer

Microstructure homogeneity and mechanical properties of laser-arc hybrid welded AZ31B magnesium alloy

The Effect of Ni Foil on the Interface Microstructure and Mechanical Properties of Laser Lap Welded Steel/mg Joint

On the heterogeneous microstructure and strengthening mechanisms in a laser welding AZ80 magnesium alloy

Effect of laser power on laser joining of carbon fiber reinforced plastic to AZ31B Mg alloy

Effect of heat input on interfacial microstructure, tensile and bending properties of dissimilar Al/steel lap joints by laser Welding-brazing

Effect of pulse overlap rate on the microstructure and mechanical properties of laser welds of thin AZ31 magnesium alloy

Investigation of interfacial microstructure and connection mechanism of magnetic field-assisted magnesium/aluminum laser welding joint

Impact of power modulation on weld appearance and mechanical properties during laser welding of AZ31B magnesium alloy

The Influence of Heat and Cryogenic Treatment on Microstructure Evolution and Mechanical Properties of Laser-Welded AZ31B

Improvement of laser welded joint properties of AZ31B magnesium alloy to DP590 dual-phase steel produced by external magnetic field

Microstructure – Properties relationship in laser-welded AZ31B magnesium alloy

Microstructure and mechanical properties of laser welding of AZ31B magnesium alloy and DP590 dual-phase steel with concave groove joint

Effect of Al Content in Magnesium Alloy on Microstructure and Mechanical Properties of Laser-Welded Mg/Ti Dissimilar Joints

Effect of preheating temperature on the microscopic structure and mechanical performance of pulsed laser welding in sheet AZ31 alloy

Investigation of the microstructure and mechanical properties of Mg–Al–Zn alloy joints formed by different laser welding processes

The influence of laser power on microstructure and properties of laser welding-brazing of Al alloys to Al-Si coated 22MnB5 steel

Effects of Laser Premelting Treatment on Microstructure and Mechanical Properties of High-Strength Steel Weld Obtained by Laser-MAG Hybrid Welding

Effect of zinc on the fracture behavior of galvanized steel/6061 aluminum alloy by laser brazing