Abstract:Developing formaldehyde-free and excellent water resistance has constantly been at the center of attention of wood adhesives. In addition to enhancing the adhesive itself, the modification of wood interface can also improve its bonding strength and water resistance. In this study, aqueous solutions of NaIO 4 and NaClO 2 have been sprayed onto the surface of poplar veneer evenly. An activated wood interface equipped with -CHO and -COOH was prepared. Traditional polyurethane adhesives are primarily two-component, with excessive manufacturing cost, complicated production and use procedures. In this study, a single component high branched polyurethane adhesive (GI) was synthesized via a A 2 +B 3 oligomerization method by using glycerol and isophorone diisocyanate (IPDI). Using branched polyamine (PA 4 N ) as a modifier, GI was modified to GI-PA 4 N , which was used as an adhesive and then hot pressed with the activated wood to make three-layer plywood. The bonding interface was equipped with urethane bonds, urea-based chemical bonds, amide bonds, Schiff bonds and hydrogen bond, which considerably enhanced the stability and water resistance of the bonding interface. FT-IR and XPS confirmed the existence of -CHO and -COOH at the interface of the activated wood, and characterized the synthesis mechanism and bonding mechanism of GI-PA 4 N . The results indicated that when the mass ratio of polyurethane to polyamine was 4:1, the overall performance of the adhesive was the best. The dry bonding strength increased from 1.92 MPa to 3.63 MPa, and the wet bonding strength increased from 1.77 MPa to 3.13 MPa, much higher than the minimum requirement of GB/T 17657–2013 (0.7 MPa). A formaldehyde-free, high-performance plywood with excellent water resistance was successfully prepared using wood interfacial activation and branched polyamine modification.

Modified high-density polyethylene film as the adhesive for veneer overlaying of wood-based panel

High-pressure Densification and Hydrophobic Coating for Enhancing the Mechanical Properties and Dimensional Stability of Soft Poplar Wood Boards

An innovative approach to manufacturing flexible decorative wood veneer using EVA film as adhesive and reinforcing materials

The use of wood veneer to beautify wood plastic composites

Easy Preparation, High Water Resistance Glucose-Based Environment-Friendly Wood Adhesives

Research Progress of Wood-Based Panels Made of Thermoplastics as Wood Adhesives

Influence of micron-sized oligomeric semisiloxane modification on surface properties of veneer and interfacial adhesion of EVA film/poplar plywood

Bonding properties of polyurethan enhanced by branched polyamine and wood interfacial activation

Investigating the influence of fabrication parameters, flax fibre reinforcement, and ageing on interlaminar shear strength in thermoplastic-bonded wood veneers

A Study on the Bonding Technology in Sliced Bamboo Veneer Manufacturing

STRUCTURAL ASSESSMENT OF LAMINATED WOOD VENEER/PLASTIC SHEET COMPOSITES USED AS BUILDING MATERIAL

Employing a mixture of fine-particle PKS, glycerol, and citric acid as an eco-friendly binder for plywood production from rubberwood (Hevea brasiliensis) veneer

Bonding performance and surface characterization of cold-bonded acetylated beech (Fagus sylvatica L.) laminated veneer lumber

Towards high performance wood composites through interface customization with cellulose-based adhesive

An Eco-Friendly Wood Adhesive Consisting of Soybean Protein and Cardanol-Based Epoxy for Wood Based Composites

Properties of patula pine plywood using phenolic resin-impregnated veneers

Preparation of highly water-resistant wood adhesives using ECH as a crosslinking agent

Adhesion performance of furfurylated plywood bonded with polyurethane and epoxy adhesives

The effect of hydroxy-methylated-resorcinol treated veneer on bonding interface and bonding strength of carbon fiber/poplar veneer composite

Novel ultrastrong wood bonding interface through chemical covalent crosslinking of aldehyde-amine

Ureido Hyperbranched Polymer Modified Urea-Formaldehyde Resin as High-Performance Particleboard Adhesive