Abstract:The pollution of contaminants brought by plastic fragments is worth paying attention in the study of microplastic. The additives, like phthalates (PAEs), introduced during manufacture, are physically dispersed and can easily release into environment. Polyvinyl chloride pipes are widely used in China, and DBP is also a typical kind of additives in PVC materials. Here, the release behavior of DBP from PVC plastic pipe fragments was investigated in water environment under different conditions. Low-density polyethylene (LDPE) passive sampler was used to monitor the contents of DBP. The curve of DBP concentration started from the first increasing stage until a short equilibrium after 45 days’ incubation followed by a second increasing part. The release kinetics and the rate-limiting step were discussed. For the whole migration period, the release process was better fitted to pseudo-second order which was participated by both intraparticle and plastic-water film diffusion processes while the two separated parts had different results. Moreover, light, smaller fragments, and higher temperature could all accelerate the release rate and increase the migration amount of DBP. The effect of temperature was the most significant of all, and higher temperature showed more significant effects. Besides, DBP tended to migrate in a long-time continuously. However, the release of additives will be promoted by various physical and chemical processes in nature compared to laboratory tests. Consequently, microplastic (plastic fragments with sizes smaller than 5 mm) with additives acts as a vector for pollutants, and will bring more threat to both environment and organisms.

What problem does this paper attempt to address?

This paper aims to explore the problem of microplastics as pollutant carriers, and specifically studies the behavior of dibutyl phthalate (DBP) released from polyvinyl chloride (PVC) pipe fragments in the water environment. The study focuses on the release kinetics of DBP from PVC pipe fragments and its limiting steps under different conditions, as well as how these conditions affect the release rate and migration amount of DBP. Through experiments, the author hopes to reveal the mechanism of microplastics as pollutant carriers in the water environment, especially the release behavior of their accompanying additives (such as DBP), so as to evaluate the potential threats of these microplastics to the environment and organisms. ### Main research contents: 1. **Release kinetics**: The kinetic process of DBP release from PVC pipe fragments was studied, and it was found that the entire release process conforms to the pseudo - second - order kinetic model, indicating that the release process involves two processes: internal particle diffusion and plastic - water interface diffusion. 2. **Limiting steps**: By analyzing different stages of the release process, it was determined that in the early stage, it is mainly controlled by plastic - water interface diffusion, and in the later stage, it is jointly affected by internal particle diffusion and interface diffusion. 3. **Influence of different conditions**: - **Illumination**: Under illumination conditions, the release rate and migration amount of DBP both increase because radiation accelerates the aging of plastics and reduces the resistance of molecular diffusion. - **Particle size**: Smaller particles have a higher specific surface area and more contact with water, resulting in an increase in DBP release. - **Temperature**: The increase in temperature significantly increases the release rate and migration amount of DBP. High temperature not only accelerates the degradation of polymers but also increases the free volume inside the polymers, making it easier for DBP to migrate into water. ### Conclusion: The research results show that microplastics (especially microplastics containing additives) can act as carriers of pollutants in the water environment, and their release behavior is affected by various factors such as illumination, particle size, and temperature. These findings emphasize the potential threats of microplastics to the environment and organisms, and suggest that further research on the additive release behavior of microplastics in the biological digestion environment is needed to comprehensively assess their risks.

Microplastic acts as a vector for contaminants: the release behavior of dibutyl phthalate from polyvinyl chloride pipe fragments in water phase