Magnesium Hydroxide as a Versatile Nanofiller for 3D-Printed PLA Bone Scaffolds

Wang Guo,Wenlang Bu,Yufeng Mao,Enyu Wang,Yanjuan Yang,Chao Liu,Feng Guo,Huaming Mai,Hui You,Yu Long

DOI: https://doi.org/10.3390/polym16020198

IF: 5

2024-01-10

Polymers

Abstract:Polylactic acid (PLA) has attracted much attention in bone tissue engineering due to its good biocompatibility and processability, but it still faces problems such as a slow degradation rate, acidic degradation product, weak biomineralization ability, and poor cell response, which limits its wider application in developing bone scaffolds. In this study, Mg(OH)2 nanoparticles were employed as a versatile nanofiller for developing PLA/Mg(OH)2 composite bone scaffolds using fused deposition modeling (FDM) 3D printing technology, and its mechanical, degradation, and biological properties were evaluated. The mechanical tests revealed that a 5 wt% addition of Mg(OH)2 improved the tensile and compressive strengths of the PLA scaffold by 20.50% and 63.97%, respectively. The soaking experiment in phosphate buffered solution (PBS) revealed that the alkaline degradation products of Mg(OH)2 neutralized the acidic degradation products of PLA, thus accelerating the degradation of PLA. The weight loss rate of the PLA/20Mg(OH)2 scaffold (15.40%) was significantly higher than that of PLA (0.15%) on day 28. Meanwhile, the composite scaffolds showed long-term Mg2+ release for more than 28 days. The simulated body fluid (SBF) immersion experiment indicated that Mg(OH)2 promoted the deposition of apatite and improved the biomineralization of PLA scaffolds. The cell culture of bone marrow mesenchymal stem cells (BMSCs) indicated that adding 5 wt% Mg(OH)2 effectively improved cell responses, including adhesion, proliferation, and osteogenic differentiation, due to the release of Mg2+. This study suggests that Mg(OH)2 can simultaneously address various issues related to polymer scaffolds, including degradation, mechanical properties, and cell interaction, having promising applications in tissue engineering.

polymer science

What problem does this paper attempt to address?

The problems that this paper attempts to solve mainly focus on improving the performance of polylactic acid (PLA) in bone tissue engineering applications. Specifically, although PLA has good biocompatibility and processability, it has the following main problems:

1. **Slow degradation rate**: The in - vivo degradation time of PLA exceeds four years, which is much slower than the time required for bone defect regeneration (several months to several years), and this is not conducive to the formation of new bone.
2. **Acidic degradation products**: The acidic products generated during the degradation of PLA may lead to aseptic inflammatory reactions.
3. **Weak bioactivity and cell response**: As an aliphatic polymer, PLA has weak bioactivity and cell response ability.
4. **Insufficient mechanical properties**: PLA needs to improve its mechanical properties to provide more stable mechanical support during bone regeneration and reconstruction.

To solve these problems, this study used magnesium hydroxide (Mg(OH)₂) nanoparticles as multifunctional fillers to prepare PLA/Mg(OH)₂ composite bone scaffolds by fused deposition modeling (FDM) 3D printing technology, and evaluated their mechanical properties, degradation properties and biological properties. The research shows that adding 5 wt% of Mg(OH)₂ can significantly improve the tensile and compressive strength of PLA scaffolds, accelerate the degradation of PLA, neutralize acidic degradation products, promote the deposition of hydroxyapatite, improve the biomineralization ability, and improve the adhesion, proliferation and osteogenic differentiation of bone marrow mesenchymal stem cells (BMSCs). These results indicate that Mg(OH)₂ can simultaneously solve multiple problems of polymer scaffolds in terms of degradation, mechanical properties and cell interactions, and has broad application prospects in tissue engineering.