Abstract:Manganese oxides with varied Mn valance states but identical morphologies were synthesized via a facile thermal treatment of γ-MnOOH. Also, their catalytic performance on ozone decomposition was investigated following the order of Mn3O4 < Mn2O3 < MnO2 < MnO2-H-200. In combination with X-ray diffraction (XRD), scanning electron microscopy (SEM), Brunauer–Emmett–Teller (BET), transmission electron microscopy (TEM), H2-temperature-programmed reduction (TPR), O2-temperature-programmed desorption (TPD), and X-ray photoelectron spectroscopy (XPS) characterization, it was deduced that the superior O3 decomposition capacity for MnO2-H-200 was strongly associated with abundant oxygen vacancies on its surface. Among Mn3O4, Mn2O3, and MnO2, the difference in O3 decomposition efficiency was dependent on the divergent nature of oxygen vacancy. Density functional theory (DFT) calculation revealed that Mn3O4 and MnO2 possessed lower formation energy of oxygen vacancy, while MnO2 had the minimum desorption energy of peroxide species (O2*). It was deduced that the promotion of the O3 decomposition capability was attributed to the easier O2* desorption. Insights into the deactivation mechanism for MnO2-H-200 further validated the assumptions. As the reaction proceeded, adsorbed oxygen species accumulated on the catalyst surface, and a portion of them were transformed to lattice oxygen. The consumption of oxygen vacancy led to the deactivation of the catalyst.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.langmuir.0c02841?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.langmuir.0c02841</a>.Catalyst preparation; catalyst characterization; XRD patterns of the as-prepared γ-MnOOH; N2 adsorption and desorption isotherms of different MnOx catalysts; top plane view and the oxygen vacancy sites of the preferentially exposed crystal plane for various MnOx during DFT calculation; FT-IR spectra of MnO2-H-200 and partially deactivate MnO2-H-200 catalysts; ozone conversion over MnO2-H-200 and the regenerated MnO2-H-200; the pore size distribution of different MnOx catalysts calculated by the BJH method (<a class="ext-link" href="/doi/suppl/10.1021/acs.langmuir.0c02841/suppl_file/la0c02841_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Different degradation mechanisms of low-concentration ozone for MIL-100(Fe) and MIL-100(Mn) over wide humidity fluctuation

Catalytic Ozonation of Multiple Vocs at Low Temperature over a Potassium-Modified Mnox-Based Catalyst

Efficient ozone decomposition in high humidity environments using novel iron-doped OMS-2-loaded activated carbon material

Exceptional Ozone Decomposition over -MnO2/AC under an Entire Humidity Environment

α-MnO 2 catalysts with efficient ozone-catalyzed decomposition under high humidity conditions

Efficient Ozone Elimination over MnO2 Via Double Moisture-Resistance Protection of Active Carbon and CeO2

Mechanism for airborne ozone decomposition on X-MIL-53(Fe) (X = H, NH2, NO2)

Insights into the Reactive and Deactivation Mechanisms of Manganese Oxides for Ozone Elimination: The Roles of Surface Oxygen Species

Interface Reconfiguration of MnCO3/Mn3O4 Heterostructure Enhances the Ozone Decomposition in the Entire Humidity Range

Highly Efficient Ozone Decomposition Against Harsh Environments over Long-Term Stable Amorphous MnOx Catalysts

Enhanced water-resistance of Mn-based catalysts for ambient temperature ozone elimination: Roles of N and Pd modification

Efficient monolithic MnOx catalyst prepared by heat treatment for ozone decomposition

Synthetic effect of supports in Cu-Mn–doped oxide catalysts for promoting ozone decomposition under humid environment

Unlocking efficient and robust ozone decomposition with CNT-confined manganese oxide via synergistic electronic modulation

Low Temperature Catalytic Ozonation of Toluene in Flue Gas over Mn-based Catalysts: Effect of Support Property and SO2/water Vapor Addition

Efficient Ozone Elimination Over MnO 2 via Double Moisture-Resistance Protection of Active Carbon and CeO 2

Enhancing ozone catalytic decomposition through acid treatment of α-MnO2 for improved activity and humidity resistance

Manganese supported on controlled dealumination Y-zeolite for ozone catalytic oxidation of low concentration toluene at low temperature

Unravelling the efficient catalytic performance of ozone decomposition over nitrogen-doped manganese oxide catalysts under high humidity

Study on the Decomposition Mechanism of Formaldehyde and Ozone Byproduct in the Presence of MnOx-TiO2 Catalyst under UV185+254nm Irradiation

Ammonium-treated birnessite-type MnO2 to increase oxygen vacancies and surface acidity for stably decomposing ozone in humid condition