Abstract:Shield method have been commonly used in water conveyance tunnels. To improve the bearing capacity of a shield tunnel under internal water pressure, a reinforced concrete lining is constructed inside the segmental linings to form a composite lining structure. However, cracks typically occur in reinforced concrete inner linings. In this study, a prototype test was performed to investigate the failure process of a composite lining. Based on the test observations, the progressive failure process of the composite lining experienced four stages. In the elastic stage, the stress and deformation of the composite lining increased linearly with the internal pressure, and no cracks appeared. In the cracking stage, cracks first occurred in the inner lining near the joints and were subsequently uniformly distributed along the circumferential direction. In the joint damage stage, the cracking of the inner lining caused more internal pressure to transmit to the segmental lining. As the internal pressure increased, compressive damage occurred in the handholes of the segmental joints. Finally, in the failure stage, the damage to the joints deteriorated and more internal pressure was borne by the rebar of the inner lining. Shear failure typically occurred at the welding point of the inner-lining rebar, followed by joint fracture near the welding point. Finally, the composite lining lost its ability. The test results showed that cracking of reinforced concrete inner lining remarkably decreased the tensile stiffness of composite lining. Consequently, the joint opening and convergence of the tunnel developed at a higher rate, posing a threat to the operational safety of the tunnel. The tensile stiffness is a key factor related to the deformation and bearing capacity of a shield tunnel. Therefore, an analytical solution was established to calculate the tensile stiffness of the composite lining after cracking. The analytical solution matched the test results well. In addition, the effects of the thickness and reinforcement ratio of the inner lining were analysed. The results suggested that increasing the reinforcement was more beneficial in improving the tensile stiffness of the composite lining.

Fiber optic sensing and performance evaluation of a water conveyance tunnel with composite linings under super-high internal pressures

In-situ Experimental Study on the Behavior of Water Conveyance Tunnel Under High Internal Pressure Using Fiber Optic Sensing Technique

INTERACTION OF SURROUNDING ROCK OR SOIL AND LINING OF A PRESSURE TUNNEL

Observed response of a shield-driven tunnel to fluctuations in river stage

Structural Behavior of Triple-Layer Composite Lining of a Water Conveyance Tunnel: Insight from Full-Scale Loading Tests

Analytical Method for Segmental Tunnel Linings Reinforced by Secondary Lining Considering Interfacial Slippage and Detachment

Interface Failure of Segmental Tunnel Lining Strengthened with Steel Plates Based on Fracture Mechanics

Aseismic Performance Analysis of Composite Lining Embedded in Saturated Poroelastic Half Space

Research on the deformation and settlement characteristics of tunnel lining structures based on distributed fibre optic sensing technology

Experimental investigation on the load-bearing capacity and deformation behaviour of the composite lining with polyurethane compressible layer

Numerical Assessment of the Structural Damage of a Composite Lining Water Conveyance Tunnel Subjected to Reverse Fault Conditions

Failure process and tensile stiffness of shield tunnel with reinforced concrete inner lining under internal water pressure

Strain analysis of tunnel lining during construction based on self-sensing monitoring technology of FRP

A novel method of imposing external water pressure to explore the failure behavior of railway tunnel linings

Diagnosis and Monitoring of Tunnel Lining Defects by Using Comprehensive Geophysical Prospecting and Fiber Bragg Grating Strain Sensor

Damage Analysis of Waterproof Layer in Composite Lining of Tunnels Based on Ritz Method

Full-scale Loading Test for Shield Tunnel Segments: Load-bearing Performance and Failure Patterns of Lining Structures

Fluid-solid coupling response of shield tunnel lining structure under high water pressure

Analysis of Mechanical Behavior of Primary Lining in Double-Arch Tunnel Based on Distributed Fibre Optic Monitoring

Failure mechanism and stiffness degradation of double lining with inner R/FRC lining subjected to internal water pressure

Life-cycle Stress Monitoring Method for Tunnel Secondary Lining Based on Distributed Optical Fiber Sensor