Effects of mechanical stress on protective properties of a marine coating on mild steel substrate

Hong-Qi Yang,Qi Zhang,Yi-Min Li,Gang Liu,Yi Huang

DOI: https://doi.org/10.1016/j.corsci.2020.108986

IF: 7.72

2020-12-01

Corrosion Science

Abstract:<p>The degradation behaviour of a marine epoxy coating on Q235 steel under mechanical stress in 3.5% NaCl solution was investigated by electrochemical impedance spectroscopy (EIS) and adhesion tests. Results revealed that mechanical stress had a significant effect on coating barrier properties, adhesion, delaminated area, water uptake and diffusion, and this effect was not only related to the magnitude and direction of stress, but depended on immersion time. The coating under mechanical stress, regardless of stress direction, deteriorated faster than that under unstressed state. The disparity in changing trends of water uptake and diffusion coefficient with mechanical stress was also discussed.</p>

materials science, multidisciplinary,metallurgy & metallurgical engineering

What problem does this paper attempt to address?

This paper attempts to address the impact of mechanical stress on the protective performance of marine epoxy coatings applied to Q235 steel substrates in a 3.5% NaCl solution. Specifically, the study aims to explore the following issues:

1. **The impact of mechanical stress on the barrier performance of the coating**: How mechanical stress affects the barrier performance of the coating, including water absorption and diffusion.
2. **The impact of mechanical stress on the adhesion of the coating**: How mechanical stress affects the adhesion between the coating and the substrate.
3. **The impact of mechanical stress on the delamination area of the coating**: How mechanical stress affects the delamination area of the coating.
4. **The impact of mechanical stress on the degradation behavior of the coating**: How mechanical stress accelerates the degradation process of the coating, and whether this impact is related to the magnitude and direction of the stress.

Through electrochemical impedance spectroscopy (EIS) and pull-off adhesion tests, the researchers conducted a detailed analysis of the changes in coating performance under different stress levels, aiming to provide theoretical basis and technical support for coating protection in practical marine engineering.