Investigation on the mechanical properties and microstructural analysis of dissimilar friction stir welding of AA5154/AA7150
Sandeep Sarnobat,Indradeep Kumar,Kuldeep Kumar Saxena,Vinayak Malik
DOI: https://doi.org/10.1080/01694243.2024.2362029
IF: 2.431
2024-06-10
Journal of Adhesion Science and Technology
Abstract:Butt welds were produced on AA5154/AA7150 using the FSW method, and measurements were taken for the hardness and elongation percentage of each joint. Regression analysis was utilized to investigate the significance of each parameter and formulate a mathematical relationship. Welding was performed at 1200 rpm, with a welding speed of 90 mm/min and a tool diameter of 28 mm, resulting in defect-free welds. Failures were commonly observed at the pin and the side of AA7150. To decrease the ultimate tensile strength (UTS), the welding speed (WS) or tool rotational speed (TRS) was increased. As both TRS and WS constitute the nugget zone, variations in hardness distribution were noted across the weld zones. ANOVA was applied in this study to establish the relative importance and influence of each factor on UTS. The ANOVA results indicated that all parameters significantly impacted UTS. Specifically, WS contributed 41.42%, diameter contributed 17.57%, and TRS contributed 13.27%. A quadratic model was also developed to describe the relationship between the factors and UTS values. Based on the data, a range of 0.41% to 10.36% differences existed between projected and actual values. The strength of the model was evaluated using R-Squared (R-Sq.), resulting in an obtained R-Sq. value of 0.892. This value indicates a robust relationship between the predicted and actual values.
materials science, multidisciplinary,engineering, chemical,mechanics