Abstract:Eutectic high entropy alloys (EHEAs) have garnered much research attention due to their excellent mechanical properties, superior castability, good oxidation resistance, and stable microstructure in a wide range of temperatures. Inspires from mature Ni and Co-based superalloys, a novel Al20Co36Cr4Fe4Ni36 EHEA was designed and prepared to obtain good mechanical properties at both room temperature and high temperatures in this study. The novel EHEA consists of a L12 phase and a B2 phase with a superior ultra-tensile strength of 1005 ± 40 MPa and a ductility of 8.8 ± 0.4% at room temperature. The engineering compressive stress–strain curves at 1073 K indicated that the current EHEA performs a high strength of 321 ± 9 MPa without fracture even at a high temperature of ~0.6 TE, which is even superior to some refractory high entropy alloys (RHEAs). The hot deformation behavior and microstructure evolution of the new EHEA was investigated at the temperature range of 1073 K to 1273 K and various strain rates from 10−3 s−1 to 10−1 s−1. The constitutive equation that describes the correlations between the flow stress, strain rate, and temperatures was constructed. Continuous dynamic recrystallization (CDRX) was the primary dynamic recrystallization (DRX) mechanism in both the L12 and B2 phases during hot deformation. However, the proportion of dynamic recrystallization grains in the L12 phase is higher than that in the B2 phase according to the high angle grain boundaries (HAGBs) under the same deformation condition, suggesting that the CDRX kinetics was faster and stronger in the L12 phase. The present study provided a new thought for designing EHEAs and an insight into the hot deformation behavior of EHEAs with lamellar morphologies.

Microstructure and properties of a novel cost-effective FeNi-based eutectic high entropy alloys

Microstructure evolution and mechanical properties of CrFeNixV0.64Ta0.36 eutectic high-entropy alloys

Microstructure and mechanical properties of Co-free AlCrFeNiTi 0.2 eutectic high-entropy alloy

Effect of Nb on microstructure and properties of AlCoCrFeNi2.1 high entropy alloy

Microstructural Evolution and Elevated-Temperature Strengthening Mechanism of Co-free FeCrMnNiV0.2Alx High-Entropy Alloys During Annealing

Effects of niobium on the microstructure, corrosion, and mechanical behavior of ultra-fine lamellar Al 0.3 CrFeCoNiNb x eutectic high-entropy alloys

Microstructure evolution and strengthening mechanisms in Ni36Co30Cr11Fe11Al12-xNbx high entropy alloys

Microstructure and mechanical properties variation with Ni content in Al0.8CoCr0.6Fe0.7Nix (x = 1.1, 1.5, 1.8, 2.0) eutectic high-entropy alloy system

Microstructure and mechanical properties of CrFeNiBx eutectic high entropy alloys

Microstructure and mechanical properties of AlCoCrFeNi2.1 eutectic high-entropy alloy synthesized by spark plasma sintering of gas-atomized powder

A novel Co-free Al0.75CrFeNi eutectic high entropy alloy with superior mechanical properties

Evolution of microstructure and mechanical properties of a novel CoCrFeNi2(TiSi)0.7 EHEA under different annealing conditions

Hot deformation characteristics and microstructure evolution of Al20Co36Cr4Fe4Ni36 eutectic high entropy alloy

Effects of Mo on microstructure and mechanical properties of Fe2Ni2CrMox eutectic high entropy alloys

Study on the strengthening mechanism of AlCoCrFeNi2.1 eutectic high-entropy alloy

Microstructure and mechanical property of novel NiAl-based hypoeutectic/eutectic/hypereutectic high-entropy alloy

Break the strength and ductility trade-off in novel NbC reinforced Fe40.5(CoCr)25Mn17.5Ni10Si5 high entropy alloy

Mechanical properties and fracture mechanism of as-cast MnFeCoCuNi high-entropy alloys

Microstructure and mechanical properties of Al-Fe-Co-Cr-Ni high entropy alloy fabricated via powder extrusion

Labyrinthine structure Al CrFeNi (x ≥ 1) eutectic high entropy alloys with duplex reinforced phases

Tensile properties and strengthening mechanisms of eutectic high-entropy alloys induced by heterostructure