Abstract:In the processing of porous ceramics, shrinkage from green body to sintered compact during drying and sintering is one of key concerns which affect microstructure and properties of the porous ceramics. Through releasing gases from the burning of the pore forming agents and volume expansion from formation of low density resultants during sintering, the sintering shrinkage can be effectively compensated and near net size preparation can be achieved. Herein, near net size porous alumina‐calcium aluminate ceramics with controllable shrinkage have been prepared by a combination of gelcasting and pore‐forming agent process through adjusting the amount of CaCO3 and polymethyl methacrylate (PMMA) microspheres added. Al2O3 and CaCO3 were used as raw material, polymethyl methacrylate (PMMA) microspheres were used as pore‐forming agent, isobutylene/maleic anhydride copolymer (Isobam104) was used as gelling agent and dispersing agent. The effects of the addition amounts of CaCO3 and PMMA in the slurry on the phase composition, shrinkage, porosity, and strength of porous alumina‐calcium aluminate ceramics were investigated. The results show that as the CaCO3 addition amount increases from 0 wt% to 20 wt%, the shrinkage of the samples gradually decreases from 7.3 % to ‐1.4 %, and the consequent porosity increases from 58 % to 66 %, while the compressive strength increases from 5.9 MPa to 15.5 MPa. When PMMA content increases from 10 wt% to 50 wt%, the shrinkage of the samples decreases first and then increases, the porosity increases from 51 % to 74 %, and the compressive strength decreases from 12.5 MPa to 5.3 MPa. The mechanisms for controlling of shrinkages during preparation of porous alumina‐calcium aluminate ceramics can be attributed to the following aspects: on one hand, gases release from burning of PMMA and decomposition of CaCO3 during sintering; on the other hand, volume expansion due to formation lower density calcium aluminates which come from the reactions between CaO and Al2O3. Near net size preparation technique is of great significance for the manufacture of porous ceramics since the subsequent machining cost can be effectively reduced.

Preparation of macroporous alumina ceramics by ice templating without freeze drying using natural rubber latex binder

Preparation of porous alumina ceramic with ultra-high porosity and long straight pores by freeze casting

The controllable microstructure of porous Al2O3 ceramics prepared via a novel freeze casting route

Natural rubber latex as a new binder for slip casting of alumina ceramics

Ceramics with Special Porous Structures Fabricated by Freeze-Gelcasting: Using tert-Butyl Alcohol as a Template

Gelcasting of alumina ceramics in the mixed acrylamide and polyacrylamide systems

High-strength porous alumina ceramics prepared from stable wet foams

Alumina Porous Ceramics Obtained by Freeze Casting: Structure and Mechanical Behaviour under Compression

Preparation of polydimethylsiloxane-coated α-alumina fillers with cold plasma for elastomer thermal interface materials

Air permeable alumina-based porous ceramics with high performance prepared by novel gel casting route

Preparation of near net size porous alumina‐calcium aluminate ceramics by gelcasting‐pore‐forming agent processs

Fabrication of Porous Alumina Ceramics with Directional Pore Channels Structure by Freeze-Gel Casting Processing

Freeze casting of aqueous alumina slurries with glycerol for porous ceramics

Porous α-Al2O3 ceramics prepared by gelcasting

High-precision and Rapid Layerless Printing Technology for High-Solid and Low-Viscosity Alumina Slurry

Design and Formulation of Polyurethane Foam Used for Porous Alumina Ceramics

Fabrication of Ceramics with Complex Porous Structures by the Impregnate–Freeze‐Casting Process

Properties of porous alumina ceramics prepared by technique combining cold-drying and sintering

Porous Alumina-Bentonite Ceramics: Effects of Fillers and Molding Technique

Freeze-Drying Defect Control of Alumina-Based Ceramic Body Prepared with Gel Casting Technology

Pore structure and thermal oxidation curing behavior of porous polymer derived ceramics with superhigh porosity fabricated by freeze casting