Aging evaluation of PEDOT:PSS films for high-efficient perovskite solar cells

DOI: https://doi.org/10.1007/s10854-023-10232-0

2023-03-15

Abstract:Perovskite solar cells have shown rapid development in efficiency since it was first produced. As a result of this development, efficiency values have reached ~ 25%. However, their efficiency decreases significantly after production. This decrease in efficiency values is called degradation or instability. Determining the source of this degradation in perovskite solar cells will also provide information on the solution of the degradation problem. For this reason, it is necessary to examine the layers that make up the perovskite solar cells separately under different aging conditions and to determine which layer or layers play an active role in the degradation. In this study, two different dopant ratio PEDOT:PSS films were produced with solution base deposition. PEDOT:PSS film's electrical conductivity changes and electronic defect states changes were determined under different atmospheric aging conditions such as laboratory atmosphere, UV aging, oxygen aging, and light soaking. Depending on these aging procedures, dark conductivity values depending on time and photoconductivity values depending on flux were recorded. Mobility-life time calculations were performed from the photoconductivity values. In the light of the obtained results, the pedot:pss film which would exhibit a more stable performance in the perovskite solar cell was decided according to the dopant ratio.

engineering, electrical & electronic,materials science, multidisciplinary,physics, condensed matter, applied