Advanced 3D Printing of Polyetherketoneketone Hydroxyapatite Composites via Fused Filament Fabrication with Increased Interlayer Connection

Krzysztof Rodzeń,Eiméar O'Donnell,Frances Hasson,Alistair McIlhagger,Brian J. Meenan,Jawad Ullah,Beata Strachota,Adam Strachota,Sean Duffy,Adrian Boyd

DOI: https://doi.org/10.3390/ma17133161

IF: 3.4

2024-06-28

Materials

Abstract:Additively manufactured implants, surgical guides, and medical devices that would have direct contact with the human body require predictable behaviour when stress is applied during their standard operation. Products built with Fused Filament Fabrication (FFF) possess orthotropic characteristics, thus, it is necessary to determine the properties that can be achieved in the XY- and Z-directions of printing. A concentration of 10 wt% of hydroxyapatite (HA) in polyetherketoneketone (PEKK) matrix was selected as the most promising biomaterial supporting cell attachment for medical applications and was characterized with an Ultimate Tensile Strength (UTS) of 78.3 MPa and 43.9 MPa in the XY- and Z-directions of 3D printing, respectively. The effect of the filler on the crystallization kinetics, which is a key parameter for the selection of semicrystalline materials suitable for 3D printing, was explained. This work clearly shows that only in situ crystallization provides the ability to build parts with a more thermodynamically stable primary form of crystallites.

materials science, multidisciplinary,metallurgy & metallurgical engineering,physics, applied,chemistry, physical, condensed matter

What problem does this paper attempt to address?

The paper mainly discusses the problem of using polyetherketoneketone (PEKK) composites with 10wt% hydroxyapatite (HA) for advanced 3D printing through the fused filament fabrication (FFF) technique. The focus of the study is on predicting the behavior of 3D printed products under stress, especially for implants, surgical guides, and medical devices that come into direct contact with the human body. The authors found that the tensile strength of the 3D printed PEKK/HA composite material is 78.3 MPa in the XY direction and 43.9 MPa in the Z direction, indicating anisotropic characteristics of the material.

The paper also investigates the influence of the filler HA on the crystallization kinetics of semi-crystalline PEKK polymers, pointing out that only in-situ crystallization can achieve a thermodynamically stable crystalline form. Furthermore, the study shows that although a high concentration of HA can improve the mechanical properties of the material, excessive content weakens the interlayer connection and affects the performance of 3D printed parts. Therefore, PEKK 6002, which has a slower crystallization rate, was chosen as a suitable material for medical applications because it can better withstand high-temperature sterilization and has higher impact toughness and strain under load.

Through experiments, the authors observed that a low concentration of HA can significantly increase the crystallization rate, while a high concentration of HA reduces this rate. The study also covers tests such as thermal stability, thermomechanical behavior, dynamic mechanical analysis (DMA), thermal gravimetric analysis (TGA), and X-ray diffraction (XRD) to evaluate the crystallinity, crystal size, and mechanical properties of the material. In conclusion, the paper emphasizes the importance of studying the crystallization kinetics of semi-crystalline materials and the performance of 3D printed parts in the Z direction, which is crucial for optimizing the 3D printed components for biomedical applications.