Influence of pyrolysis parameters on phosphorus fractions of biosolids derived biochar
S Adhikari,G Gascó,A Méndez,A Surapaneni,V Jegatheesan,K Shah,J Paz-Ferreiro,S. Adhikari,G. Gascó,A. Méndez,A. Surapaneni,V. Jegatheesan,K. Shah,J. Paz-Ferreiro
DOI: https://doi.org/10.1016/j.scitotenv.2019.133846
2019-12-01
Abstract:<p>Transforming biosolids into biochar, through pyrolysis, could result in more sustainable waste management. Influence of pyrolysis conditions (temperature, heating rate and residence time) on physico-chemical properties of biosolids (collected at Mount Martha Water Recycling Plant, Melbourne), phosphorus fractions and phosphorus forms was investigated. Twelve different biochar samples were produced at 400, 500 and 600 °C, at two heating rates (5 and 20 °C/min) and at two residence times (30 and 120 min). Biochar yield, pH, electrical conductivity (EC), elements (C, H and N) and BET surface area were analysed. Sequential extraction of P in biosolids and resultant biochars was done using Hedley method. Characterization was completed with SEM images and results from <sup>31</sup>P liquid state NMR. Increased temperatures would not only increase the alkalinity, decrease EC and increase the adsorption capacity by increasing the surface area but also convert the readily available P to a less available pool. Therefore, this nutrient might be released to soil slowly over a longer period of time. The results showed that temperature, along with residence time and heating rate, had a significant effect on the characteristics observed. Therefore, all these factors need to be carefully considered when preparing biochar for use as a soil amendment.</p>
environmental sciences