Post-fire Performance of Wire-arc-Sprayed Zn-15Al Coatings

Ratna Divya Yasoda,Ying Huang,Ravi Kiran,Xiaoning Qi

DOI: https://doi.org/10.1007/s11666-023-01577-3

IF: 2.839

2023-03-23

Journal of Thermal Spray Technology

Abstract:Wire-arc-sprayed Zn-15Al coatings are used to mitigate corrosion in steel infrastructure such as pipelines, offshore platforms, and bridges that are susceptible to fire due to the handling of flammable products and wildfire events. Past studies indicate that steel retains its engineering properties when exposed to fire temperatures up to 600 °C. Therefore, this paper aims to assess the performance of Zn-15Al protective coatings after being subjected to a fire accident. For this purpose, coated steel plates were subjected to temperatures ranging from 300 °C to failure at 100 °C intervals in a furnace simulating the fire accidents. Post-fire microstructural characterization, mechanical integrity tests, and electrochemical studies were performed on the coating. The coating was intact primarily when cooled from 500 °C due to limited high-temperature oxidation and formation of intermetallic phases of zinc and aluminum including eutectoid (α + η), partially converted eutectic (β + η) and a zinc-rich η-phase. These changes in the coating microstructure resulted in increased microhardness and consistent wear loss and an increase in the coating's electrochemical impedance compared to its as-deposited condition favoring the reusability of the coated steel members. However, at 600 °C the presence of large quantities of oxidation products increased the porosity and decreased the mechanical properties of the coating. Furthermore, the separation of the zinc-rich matrix from the coating occurred and made the cross section look like galvanized steel retaining corrosion protection ability. Micro-cracks indicating coating failure were noticed when cooled from 700 °C exposure, and hence the Zn-15Al coatings should be replaced when temperatures exceed 600 °C.

materials science, coatings & films