Structural Characterization, Dielectric Properties, Corrosion Resistance, and In Vitro Thrombogenicity of Zinc-Fabricated Hydroxyapatite Implants

Anuradha Mahanty,Deep Shikha

DOI: https://doi.org/10.1007/s11665-023-08054-6

IF: 2.3

2023-03-21

Journal of Materials Engineering and Performance

Abstract:Zinc-fabricated hydroxyapatite (ZnHAp) of different weight percent was prepared using solgel method. The paper illustrates on how zinc ion substitution effects the phase, the functional group shifting, its morphology, the mechanical properties, in vitro corrosion behavior, and dielectric properties. The amount of zinc incorporated in the lattice was studied using ICP, and pore size was calculated from BET. Thrombogenic studies were done using whole blood clotting assay method. From the EDX study, Ca/P ratio was found to be in the range of 1.5 to 1.67. The XRD and Raman spectra clearly revealed the incorporation of zinc in HAp matrix. Initially, the XRD peaks showed a decrease in the intensity, and then with an increase in the concentration of Zn, the intensity of the peaks increased. The crystallite size decreased with an increase in zinc concentration up to 2 wt.% ZnHAp, followed by an increase in the crystallite size up to 4 wt.% ZnHAp. With an increase in the zinc concentration, the hardness of the doped samples was also found to increase. It was observed that there was an improvement in corrosion resistance when zinc was incorporated in the HAp matrix. The corrosion was mainly at grain boundaries. The ZnHAp samples showed a decrease in impedance with an increase in the frequency, implying better conductivity of the samples. The pore size of the samples was found to be in the nanometer range without showing any gradual change. The ZnHAp samples showed moderate blood clotting tendency.

materials science, multidisciplinary