Abstract:A magnesium-based metal–organic framework (Mg-MOF-74) exhibits excellent CO2 adsorption under ambient conditions. However, the photostability of Mg-MOF-74 for CO2 adsorption is poor. In this study, MgxCu1–x-MOF-74 was synthesized by using a facile “one-pot” method. Furthermore, the effects of synthesis conditions on the CO2 adsorption capacity were investigated comprehensively. X-ray diffraction, Fourier transform infrared, scanning electron microscopy, thermo gravimetric analysis, inductively coupled plasma atomic emission spectroscopy, ultraviolet–visible spectroscopy and photoluminescence spectroscopy, and CO2 static adsorption–desorption techniques were used to characterize the structures, morphology, and physicochemical properties of MgxCu1–x-MOF-74. CO2 uptake of MgxCu1–x-MOF-74 under visible light illumination was measured by the CO2 static adsorption test combined with the Xe lamp. The results revealed that MgxCu1–x-MOF-74 exhibited excellent photocatalytic activity. Furthermore, the CO2 adsorption capacity of MgxCu1–x-MOF-74 was excellent at a synthesis temperature and time of 398 K and 24 h in dimethylformamide (DMF)-EtOH-MeOH mixing solvents, respectively. MgxCu1–x-MOF-74 retained a crystal structure similar to that of the corresponding monometallic MOF-74, and its CO2 uptake under visible light was superior to that of the corresponding monometallic MOF-74. Particularly, the CO2 uptake of Mg0.4Cu0.6-MOF-74 under Xe lamp illumination for 24 h was the highest, up to 3.52 mmol·g–1, which was 1.18 and 2.09 times higher than that of Mg- and Cu-MOF-74, respectively. The yield of the photocatalytic reduction of CO2 to CO was 49.44 μmol·gcat–1 over Mg0.4Cu0.6-MOF-74 under visible light for 8 h. Mg2+ and Cu2+ functioned as open alkali metal that could adsorb and activate CO2. The synergistic effect between Mg and Cu metal strengthened MgxCu1–x-MOF-74 photostability for CO2 adsorption and broadened the scope of its photocatalytic application. The “bimetallic” strategy exhibits considerable potential for use in MOF-based semiconductor composites and provides a feasible method for catalyst design with remarkable CO2 adsorption capacity and photocatalytic activity.

Preparation and characterization of Bimetal MOF-74-Co/Cu and its toluene adsorption performances

Synthesis of bimetallic–organic framework Cu/Co-BTC and the improved performance of thiophene adsorption

Stable effect on MIL-101(Cr) with Cu2+ for the toluene adsorption

Bimetal oxide CuO/Co3O4 derived from Cu ions partly-substituted framework of ZIF-67 for toluene catalytic oxidation

Synthesis and application of Cu-BTC@ZSM-5 composites as effective adsorbents for removal of toluene gas under moist ambience: kinetics, thermodynamics, and mechanism studies

Controllable synthesis of Co-MOF-74 catalysts and their application in catalytic oxidation of toluene

Catalytic oxidation of toluene over Co-Cu bimetallic oxides derived from CoyCu3-y-MOF-74

Study on the adsorption performance of toluene by bimetallic doped MOFs with high adsorption capacity

Efficient adsorptive removal of dibenzothiophene from model fuels by encapsulated of Cu+ and phosphotungstic acid (PTA) in Co-MOF

Preparation of 26-facet Cu2O@Cu composite and its methyl orange adsorption behavior

CO2 Adsorption of Metal Organic Framework Material Cu-BTC via Different Preparation Routes

Significant Gas Adsorption and Catalytic Performance by a Robust Cu(II) -MOF Derived through Single-Crystal to Single-Crystal Transmetalation of a Thermally Less-Stable Zn(II) -MOF

One-Pot Method Synthesis of Bimetallic MgCu-MOF-74 and Its CO2 Adsorption under Visible Light

Adsorption study of CO2, CH4, N2, and H2O on an interwoven copper carboxylate metal-organic framework (MOF-14)

Tuning 1-Hexene/n-hexane Adsorption on MOF-74 Via Constructing Co-Mg Bimetallic Frameworks

Core-shell Co-MOF-74@Mn-MOF-74 catalysts with Controllable shell thickness and their enhanced catalytic activity for toluene oxidation

The preparation of defective UiO-66 metal organic framework using MOF-5 as structural modifier with high sorption capacity for gaseous toluene

The introduction of nitrogen-containing heterocyclic compounds (NHC) and Cu 2+ in Co-MOF further improves the removal of dibenzothiophene from model fuels

Highly Stable MOFs-Derived Cu–Co Composite Metal Oxides for Catalytic Oxidation of Toluene

CO2 and N2 adsorption and separation using aminated UiO-66 and Cu3(BTC)2: A comparative study

Adsorption of Carbon Dioxide, Methane and Nitrogen on an Ultramicroporous Copper Metal-Organic Framework.