The preparation of defective UiO-66 metal organic framework using MOF-5 as structural modifier with high sorption capacity for gaseous toluene

Xiaodong Zhang,Xiaoyu Shi,Jinfeng Chen,Yang Yang,Guang Lu

DOI: https://doi.org/10.1016/j.jece.2019.103405

IF: 7.7

2019-10-01

Journal of Environmental Chemical Engineering

Abstract:In this work, modified defective UiO-66 was successfully synthesized using another MOF (MOF-5) as structural modifier. Some analytical techniques such as X-ray diffraction (XRD), scanning electron microscopy (SEM), N2 adsorption-desorption isotherms and thermogravimetric (TG) had been used to characterize pristine and modified UiO-66. Moreover, static adsorption tests, dynamic adsorption tests and toluene temperature programmed desorption (TPD) measurement had been used to explore toluene adsorption/desorption capacity and kinetics. It was found that the modified material (M-U-0.01) formed a certain number of defects when the MOF-5/Zr4+ ratio was 0.01, which was conducive to toluene adsorption. The M-U-0.01 (257 mg g−1) demonstrated 1.7 times toluene sorption property of the pristine UiO-66 (151 mg g−1). The interactions between toluene and pristine and modified MOFs were analyzed through the isosteric adsorption heat (ΔHads) and the Henry's law constant (KH), indicating that toluene molecules and M-U-0.01 had a strong interaction. The effect of relative humidity and temperature on the toluene sorption property was further studied. Modified defective UiO-66 displayed good thermal stability and reproducibility.

engineering, chemical, environmental